SABIC Innovative Plastics Valox® 735 PBT (Asia Pacific)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® 735 PBT (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
40% glass/mineral, excellent thermal performance/low shrink. Motorized heating appliances, adaptor rings, oven grills, etc. Black/natural only.
Physical Properties Metric English Comments
Specific Gravity 1.62 g/cc
1.62 g/cc
ASTM D792
Water Absorption 0.070 %

@Time 86400 sec
0.070 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0030 - 0.0040 cm/cm

@Thickness 1.50 - 3.20 mm
0.0030 - 0.0040 in/in

@Thickness 0.0591 - 0.126 in
SABIC Method
0.0040 - 0.0060 cm/cm

@Thickness 3.20 - 4.60 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 - 0.181 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 1.50 - 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.0591 - 0.126 in
SABIC Method
0.0060 - 0.0080 cm/cm

@Thickness 3.20 - 4.60 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 - 0.181 in
SABIC Method
Mechanical Properties Metric English Comments
Hardness, Rockwell R 109
109
ASTM D785
Tensile Strength at Break 75.0 MPa
10900 psi
Type I, 5 mm/min; ASTM D638
Flexural Strength 124 MPa
18000 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 8.27 GPa
1200 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.740 J/cm
1.39 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.27 J/cm
8.00 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
14.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
25.2 µm/m-°C

@Temperature 60.0 - 138 °C
14.0 µin/in-°F

@Temperature 140 - 280 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 215 °C

@Thickness 6.40 mm
419 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 198 °C

@Thickness 6.40 mm
388 °F

@Thickness 0.252 in
unannealed; ASTM D648
UL RTI, Electrical 140 °C
284 °F
UL 746B
UL RTI, Mechanical with Impact 140 °C
284 °F
UL 746B
UL RTI, Mechanical without Impact 140 °C
284 °F
UL 746B
Flammability, UL94 HB

@Thickness 0.810 mm
HB

@Thickness 0.0319 in
UL 94
Electrical Properties Metric English Comments
Volume Resistivity 1.30e+15 ohm-cm
1.30e+15 ohm-cm
ASTM D257
Dielectric Constant 4.0

@Frequency 1.00e+6 Hz
4.0

@Frequency 1.00e+6 Hz
ASTM D150
4.3

@Frequency 100 Hz
4.3

@Frequency 100 Hz
ASTM D150
Dielectric Strength 23.6 kV/mm

@Thickness 3.20 mm
599 kV/in

@Thickness 0.126 in
in air; ASTM D149
29.5 kV/mm

@Thickness 1.60 mm
749 kV/in

@Thickness 0.0630 in
in oil; ASTM D149
Dissipation Factor 0.0010

@Frequency 100 Hz
0.0010

@Frequency 100 Hz
ASTM D150
0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
ASTM D150
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index 250 - 400 V
250 - 400 V
UL 746A
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
UL 746A
High Amp Arc Ignition, HAI 15 - 30 arcs
15 - 30 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 10.0 - 25.4 mm/min
0.394 - 1.00 in/min
UL 746A
Descriptive Properties Value Comments
Specific Volume 0.62cm^3/g
ASTM D792