Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 5.00 MPa | 725 psi | ISO 37 |
PolyOne OnFlex™ S EH 60A-3S7003 Thermoplastic Elastomer (TPE) OnFlex™-S EH thermoplastic elastomer compounds are based on hydrogenated styrenic block copolymers. This range of compounds are formulated to deliver a great cost/performance ratio in addition to t.. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ISO 37 |
PolyOne OnFlex™ S EH 70A-3S7004 Thermoplastic Elastomer (TPE) OnFlex™-S EH thermoplastic elastomer compounds are based on hydrogenated styrenic block copolymers. This range of compounds are formulated to deliver a great cost/performance ratio in addition to t.. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ISO 37 |
Huntsman AVALON® 650 B Thermoplastic Polyurethane Performance Features: AVALON® injection molding products are trusted worldwide to deliver:Outstanding flex performanceExcellent slip resistancePerfect surface definitionTransparency and transluce.. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCP700 PPE-TPE (Europe-Africa-Middle East) Flexible PPE-TPE injection grade suitable for over-molding applications such as plugs, strain relief's, and connectors. Good processability. 70 Shore A hardness. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP MX95318 PP LNP* THERMOCOMP* MX95318 is a compound based on Polypropylene containing Proprietary Filler(s). |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ASTM D412 |
Teknor Apex Monprene® MP-1959G Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ISO 37 |
ELASTO UK Dryflex® 3006-101 TPE, Modified Injection Molding Grade for Auto Interior Parts The VTC TPE Group have developed endless formulations to fulfill different properties and application requirements to optimize the finished component. VTC Dryflex® 3006-101 is specifically designe.. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ASTM D638 |
ELASTO UK Dryflex® 502400S SEBS Based Material, Unfilled Qualities, 40A Hardness, Black The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha.. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | Across Flow; ASTM D412 |
ExxonMobil Santoprene® 121-58W175 Thermoplastic Elastomer A soft, black, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance, and is designed for .. |
|||
Tensile Strength at Break | >= 5.00 MPa | >= 725 psi | ISO R 527 |
Fainplast Compounds CR 0118 Flexible PVC, Electrical Bedding Easy strip bedding |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ISO R 527 |
Fainplast Compounds GS 38/T Flexible PVC, Injection Molding for Transparent Technical Items Dolls |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ASTM D638 |
Azdel SuperLite® SL552000-100 PP Resin Matrix / 55% Glass Fiber (12 mm Molded Thickness) AZDEL SuperLite® SL552000-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ISO 527-1 |
Barlog Plastics KEBAFLEX E 60.1 TPE-V, Shore A60 TPE-VInformation provided by BARLOG plastics GmbH. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ASTM D638 |
Arkema Group EVATANE® 42-60 Copolymer Ethylene - Vinyl Acetate EVATANE 42-60 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerisation process. EVATANE 42-60 is stabilized with antioxidants and contains slip and antibloc.. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ISO 527 |
Breplast Bretene SP Polypropylene / Polyethylene Composite Recovered polypropylene and polyethylene compositeInformation provided by Breplast S.p.A. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | |
LATI Latimass 53-04 D008 PP Homopolymer, Impact Modified Specific density compound based on Polypropylene homopolymer (PPh), impact modified. Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation.. |
|||
Tensile Strength at Break | 5.00 MPa | 725 psi | ISO R 527 |
Fainplast Compounds PM 50/C Flexible PVC, Extrusion Gaskets for frames |