- HOME
- POLYMER SEARCH
- Polymer Property : Cure Time = 7200 min
Polymer Property : Cure Time = 7200 min Product List
Processing PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 7200 - 10100 min @Temperature 25.0 °C |
120 - 168 hour @Temperature 77.0 °F |
|
| Henkel Hysol EA 9321 Paste Adhesive System Thixotropic adhesive that yields tough, durable bonds over a wide temperature range.Applications: Potting Structural Repair |
|||
| Cure Time | 7200 - 10100 min @Temperature 25.0 °C |
120 - 168 hour @Temperature 77.0 °F |
|
| Henkel Hysol EA 9330.3 Paste Adhesive System Non-slump, thixotropic adhesive with high peel strength and excellent environmental durability.Applications:Structural Repair Composite Bonding |
|||
| Cure Time | 7200 - 10100 min @Temperature 25.0 °C |
120 - 168 hour @Temperature 77.0 °F |
|
| Henkel Hysol EA 9309.3NA Paste Adhesive System Toughened adhesive with excellent peel strength. Contains glass beads for bond line control.Applications: Structural Repair Composite Bonding |
|||
| Cure Time | 7200 - 10100 min @Temperature 25.0 °C |
120 - 168 hour @Temperature 77.0 °F |
|
| Henkel Hysol EA 934NA Paste Adhesive System Two part adhesive system with superior strengthCures at room temperatureApplications: Potting Structural Repair Liquid Shim |
|||
| Cure Time | 7200 - 10100 min @Temperature 25.0 °C |
120 - 168 hour @Temperature 77.0 °F |
|
| Henkel Hysol EA 9359.3 Paste Adhesive System Excellent peel and shear strength. Bonds a variety of substrates.Applications: Structural Repair Composite Bonding |
|||
| Cure Time | 7200 - 10100 min @Temperature 25.0 °C |
120 - 168 hour @Temperature 77.0 °F |
|
| Henkel Hysol EA 9360 Paste Adhesive System Structural adhesive, exhibits excellent peel strength, tensile lap shear strength.Applications: Structural Repair Composite Bonding Liquid Shim |
|||
| Cure Time | 7200 - 10100 min @Temperature 25.0 °C |
120 - 168 hour @Temperature 77.0 °F |
|
| Henkel Hysol EA 9377 Paste Adhesive System Moldable plastic shim, excellent microcracking resistance under thermal cycling. High compressive strength.Application: Liquid Shim |
|||
| Cure Time | 7200 - 10100 min @Temperature 23.0 °C |
120 - 168 hour @Temperature 73.4 °F |
|
| Master Bond EP29LP Low Exotherm, Low Viscosity Two Component Epoxy System Master Bond Polymer System EP29LP is a two component high performance epoxy resin system featuring low viscosity, long pot life and low exotherm. As an adhesive this versatile material will form bon.. |
|||
| Cure Time | 7200 - 10100 min @Temperature 23.0 °C |
120 - 168 hour @Temperature 73.4 °F |
|
| Master Bond EP37-3 Optically Clear, Impact Resistant Two Component Epoxy Master Bond Polymer System EP37-3 is a low viscosity, resilient, optically clear two component epoxy resin system designed for high performance bonding, coating and casting applications. As an adhes.. |
|||
| Cure Time | 7200 min @Temperature 23.0 °C |
120 hour @Temperature 73.4 °F |
|
| Tra-Con Tra-Bond 216C02 Encapsulating Adhesive TRA-BOND 216C02 is a semi-flexible, two-part gray encapsulant. It readily bonds to glass, ceramics, most metals, many plastics and other common electronic materials. The fully cured adhesive is an e.. |
|||
| Cure Time | 7200 - 10100 min @Temperature 23.0 °C |
120 - 168 hour @Temperature 73.4 °F |
|
| Master Bond EP29LPSP Low Outgassing, Optically Clear Two Component Epoxy Master Bond Polymer System EP29LPSP is a two component, high performance, modified low temperature heat cured epoxy system specially formulated for cryogenic applications. EP29LPSP is serviceable at.. |
|||
| Cure Time | 7200 min @Temperature 32.0 °C |
120 hour @Temperature 89.6 °F |
Full Chemical |
| Chesterton ARC 791 Composite Description: A quartz reinforced composite designed to resurface and restore concrete surfaces, to protect new concrete, and to repair concrete damaged by chemical and physical abuse. ARC 791 has ex.. |
|||
| Cure Time | 7200 min @Temperature 32.0 °C |
120 hour @Temperature 89.6 °F |
Full Chemical |
| Chesterton ARC 988 Composite Description: A high performance, quartz reinforced composite designed to resurface and restore concrete surfaces, to protect new concrete, and to repair concrete damaged by severe chemical and physi.. |
|||
| Cure Time | 7200 min @Temperature 32.0 °C |
120 hour @Temperature 89.6 °F |
Full Chemical |
| Chesterton ARC PW Potable Water Coating Description: ARC PW is a 100% solids lining certified for NSF/ANSI 61 potable water, cold water service. It is recommended to be applied by brush, roll or spray at 500-750 microns (20-30 mils) total.. |
|||
| Cure Time | 7200 min @Temperature 32.0 °C |
120 hour @Temperature 89.6 °F |
Full Chemical |
| Chesterton ARC S1 General purpose coating Description: An advanced polymer composite formulated to protect metal surfaces from corrosion and chmical attack. It is normally applied at a thickness of 250 microns (10 mils) per coat. Non-shrink.. |
|||
| Cure Time | 7200 min @Temperature 10.0 °C |
120 hour @Temperature 50.0 °F |
Full Chemical |
| Chesterton ARC SD4i High temperature ceramic reinforced erosion resistant coating Description: An advanced ceramic composite for resurfacing and protection of metal surfaces in immersion service. It is normally applied in a thickness range of 250-370 microns (10-15 mils) per coat.. |
|||
| Cure Time | 7200 min @Temperature 10.0 °C |
120 hour @Temperature 50.0 °F |
Full Chemical |
| Chesterton MRS S2 Metal Rebuilding System An advanced ceramic composite for the resurfacing and protection of all metal surfaces. It is normally applied at a thickness of 250 microns (10 mils) per coat. Non-shrinking, 100% solids. MRS S2 is.. |
|||
| Cure Time | 7200 min @Temperature 25.0 °C |
120 hour @Temperature 77.0 °F |
|
| Cytec Conathane® CC-1155-35 (Conap) Polyurethane Two-component Dielectric Conformal Coating Dielectric Conformal Coatings for ElectronicsCytec dielectric conformal coatings are the most widely used conformal coatings in industry today for such divergent applications as aircraft avionics, i.. |
|||
| Cure Time | 7200 min @Temperature 16.0 °C |
120 hour @Temperature 60.8 °F |
Full Mechanical |
| Chesterton ARC HT-S High Temperature Corrosion Resistant Coating Description: ARC HT-S is a high temperature corrosion resistant coating for continuous operating conditions at elevated temperatures. It is easily applied by brush or roller and can be sprayed with .. |
|||
| Cure Time | 7200 min @Temperature 16.0 °C |
120 hour @Temperature 60.8 °F |
Full Chemical |
| Chesterton ARC HT-S High Temperature Corrosion Resistant Coating Description: ARC HT-S is a high temperature corrosion resistant coating for continuous operating conditions at elevated temperatures. It is easily applied by brush or roller and can be sprayed with .. |
|||
| Cure Time | 7200 - 10080 min @Temperature 15.556 - 26.667 °C |
120 - 168.0 hour @Temperature 60.001 - 80.001 °F |
(5-7 Days) |
| Abatron AboTar 8101-8 Solventless Tar-Epoxy Compound AboTar 8101-8 is a 2-part tar-epoxy variable-ratio system. It is weather- and water-proof, flexible, and acid, alkali, and fuel resistant. It can be used neat or with sand or aggregates. Uses: Resu.. |
|||
| Cure Time | 7200 min @Temperature 21.0 °C |
120 hour @Temperature 69.8 °F |
Full Cure, 50% RH |
| 3M 5200 Marine Adhesive/Sealant 3M™ Marine Adhesive/Sealant 5200 is a one-part polyurethane that chemically reacts with moisture to deliver strong, flexible bonds. It has excellent adhesion to wood, gelcoat and fiberglass. It for.. |
|||
| Cure Time | 7200 - 10080 min @Temperature 24.0 °C |
120 - 168.0 hour @Temperature 75.2 °F |
full cure |
| BCC Products BC 8782 Urethane Casting BC 8782 produces a high impact rigid 82 Shore D material that is commonly used to make clear or tinted castings of all kinds. When used at room temperature castings 1/8" thick or larger can be readi.. |
|||
| Cure Time | 7200 - 10080 min @Temperature 24.0 °C |
120 - 168.0 hour @Temperature 75.2 °F |
complete cure |
| BCC Products BC 8880 Polyurethane Elastomer Surface Coat BC8880 is a two-part urethane gel coat which exhibits excellent handling characteristics and very low moisture sensitivity. Its characteristics include a high modulus and a high hardness. It is a br.. |
|||
| Cure Time | 7200 - 10100 min @Temperature 25.0 °C |
120 - 168 hour @Temperature 77.0 °F |
|
| Henkel Hysol EA 9313 Paste Adhesive System Very low viscosity adhesive yielding tough, flexible bonds. Injectable. |
|||
| Cure Time | 7200 - 10100 min @Temperature 25.0 °C |
120 - 168 hour @Temperature 77.0 °F |
|
| Henkel Hysol EA 9323 Paste Adhesive System Viscous, but pourable, liquid adhesive that yields tough, durable adhesive bonds over a wide temperature range.Application: Structural Repair |
|||
| Cure Time | 7200 - 10100 min @Temperature 25.0 °C |
120 - 168 hour @Temperature 77.0 °F |
|
| Henkel Hysol EA 9394 Paste Adhesive System Thixotropic adhesive with structural properties to 350°F / 177°C.Applications: Potting Structural Repair Composite Bonding Liquid Shim |
|||
| Cure Time | 7200 - 10100 min @Temperature 25.0 °C |
120 - 168 hour @Temperature 77.0 °F |
|
| Henkel Hysol EA 9395 Paste Adhesive System Two-part, nonmetallic-filled version of Hysol EA 9394.Applications: Potting Structural Repair Composite Bonding |
|||
| Cure Time | 7200 - 10100 min @Temperature 25.0 °C |
120 - 168 hour @Temperature 77.0 °F |
|
| Henkel Hysol EA 9396 Paste Adhesive System Two-part, low viscosity, unfilled version of Hysol EA 9394. Qualified to BMS 8-301.Applications: Structural Repair Low Viscosity Wet Lay-Up Composite Bonding |
|||
| Cure Time | 7200 - 10100 min @Temperature 25.0 °C |
120 - 168 hour @Temperature 77.0 °F |
|
| Henkel Hysol EA 956 Paste Adhesive System Very low viscosity, cures at room temperatureDesigned for wet lay-up repairApplications: Structural Repair Low Viscosity Wet Lay-Up |
|||