ALM PA 650 Nylon 12 SLS Prototyping Polymer

Category Polymer , Rapid Prototyping Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer ALM Advanced Laser Materials
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ALM PA 650 Nylon 12 SLS Prototyping Polymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Combines strength, durability (high impact) and chemical resistance and produces strong, durable, end use prototype parts. SL parts are less porous, more precise and have less noticeable build lines than FDM (Fused Deposition Modeling) parts. LS systems build in 0.004-0.006 inch layers.Information provided by Axis Prototypes.
Physical Properties Metric English Comments
Bulk Density 0.460 g/cc
0.0166 lb/in³
ASTM D1895
Density 1.02 g/cc
0.0368 lb/in³
Sintered Part; ASTM D792
Particle Size 55 µm
55 µm
Average D50; Laser Diffraction
30 - 100 µm
30 - 100 µm
Range (D10 to D90); Laser Diffraction
Melt Flow 50 g/10 min

@Load 5.00 kg,
Temperature 235 °C
50 g/10 min

@Load 11.0 lb,
Temperature 455 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 48.0 MPa
6960 psi
XY direction; ASTM D638
Elongation at Break 24 %
24 %
XY direction; ASTM D638
Tensile Modulus 1.70 GPa
247 ksi
XY direction; ASTM D638
Flexural Modulus 1.50 GPa
218 ksi
XY direction; ASTM D790
Izod Impact, Notched 2.20 J/cm
4.12 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.40 J/cm
8.24 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Melting Point 181 °C
358 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 177 °C
351 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C
187 °F
ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 3.10e+14 ohm-cm
3.10e+14 ohm-cm
50% RH; 500V; ASTM D257
Surface Resistance 3.00e+14 ohm
3.00e+14 ohm
50% RH; 500V; ASTM D257
Dielectric Constant 2.9
2.9
50% RH; 500V; ASTM D150
Descriptive Properties Value Comments
Color White