Abatron AboCast/AboCure 8502-1 Epoxy

Category Polymer , Thermoset , Epoxy , Epoxy, Cast, Unreinforced
Manufacturer Abatron
Trade Name AboCast/AboCure
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Abatron AboCast/AboCure 8502-1 Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AboCast/AboCure 8502-1 is a solventless clear Epoxy System, used as a casting, adhesive, and impregnating resin for transformers, capacitors, coils, and other electronic components requiring a low-viscosity, flexibilized resin with long pot life. It is also available in colors and in filled form. It is easy to use and its shelf life is virtually indefinite.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0420 lb/in³
Water Absorption 0.30 - 0.40 %

@Time 864000 sec
0.30 - 0.40 %

@Time 240 hour
Viscosity 46 cP

@Temperature 65.0 °C
46 cP

@Temperature 149 °F
Mechanical Properties Metric English Comments
Hardness, Rockwell M 85
85
Tensile Strength, Ultimate 67.6 MPa
9800 psi
Elongation at Break 1.7 %
1.7 %
Elongation at Yield 4.7 %
4.7 %
Tensile Modulus 5.86 GPa
850 ksi
Flexural Strength 64.8 MPa
9400 psi
Flexural Modulus 2.07 GPa
300 ksi
Compressive Yield Strength 103 MPa
15000 psi
Compressive Modulus 3.34 GPa
485 ksi
Izod Impact, Notched 0.320 J/cm
0.600 ft-lb/in
Thermal Properties Metric English Comments
CTE, linear 60.0 - 65.0 µm/m-°C
33.3 - 36.1 µin/in-°F
Thermal Conductivity 0.167 - 0.201 W/m-K
1.16 - 1.39 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air 49.0 °C
120 °F
Deflection Temp at unknown load
Electrical Properties Metric English Comments
Volume Resistivity 2.50e+15 ohm-cm
2.50e+15 ohm-cm
Cond. C (96 hrs/23°C/96% rel. humidity)
5.10e+15 ohm-cm
5.10e+15 ohm-cm
Cond. A (as received)
Surface Resistance 2.70e+14 ohm
2.70e+14 ohm
Cond. C
2.80e+14 ohm
2.80e+14 ohm
Cond. A
Dielectric Constant 3.23

@Frequency 1.00e+6 Hz
3.23

@Frequency 1.00e+6 Hz
Cond. A (as received)
3.32

@Frequency 1.00e+6 Hz
3.32

@Frequency 1.00e+6 Hz
Cond. D (48 hrs. in dist. H2O at 50°C)
3.44

@Frequency 1000 Hz
3.44

@Frequency 1000 Hz
Cond. A (as received)
3.47

@Frequency 60.0 Hz
3.47

@Frequency 60.0 Hz
Cond. A (as received)
3.93

@Frequency 1000 Hz
3.93

@Frequency 1000 Hz
Cond. D (48 hrs. in dist. H2O at 50°C)
4.16

@Frequency 60.0 Hz
4.16

@Frequency 60.0 Hz
Cond. D (48 hrs. in dist. H2O at 50°C)
Dissipation Factor 0.0070

@Frequency 1000 Hz
0.0070

@Frequency 1000 Hz
Cond. A (as received)
0.0079

@Frequency 60.0 Hz
0.0079

@Frequency 60.0 Hz
Cond. A (as received)
0.026

@Frequency 1.00e+6 Hz
0.026

@Frequency 1.00e+6 Hz
Cond. A (as received)
0.032

@Frequency 1000 Hz
0.032

@Frequency 1000 Hz
Cond. D (48 h. in dist. H2O at 50°C)
0.045

@Frequency 1.00e+6 Hz
0.045

@Frequency 1.00e+6 Hz
Cond. D (48 h. in dist. H2O at 50°C)
0.055

@Frequency 60.0 Hz
0.055

@Frequency 60.0 Hz
Cond. D (48 h. in dist. H2O at 50°C)
Processing Properties Metric English Comments
Cure Time 120 - 180 min

@Temperature 150 - 160 °C
2.00 - 3.00 hour

@Temperature 302 - 320 °F
960 min

@Temperature 95.0 °C
16.0 hour

@Temperature 203 °F
Pot Life 420 min

@Temperature 65.0 °C
420 min

@Temperature 149 °F
2880 min

@Temperature 20.0 °C
2880 min

@Temperature 68.0 °F
Descriptive Properties Value Comments
Deflection at Break 0.53 in.
Parts by Weight (pbw) 100
AboCast
88
AboCure