- Aremco Ceramabond™ 835-MB High Temperature Ceramic Adhesive/Paste, Alumina Filled
Aremco Ceramabond™ 835-MB High Temperature Ceramic Adhesive/Paste, Alumina Filled
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Aremco |
| Trade Name | Ceramabond™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Ceramabond™ 835-MB High Temperature Ceramic Adhesive/Paste, Alumina Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and do not outgas after curing. They are also environmentally safe, non-flammable materials which contain no volatile organic compounds.General Features: High Strength, Good Filler Bonding: Ceramic to Ceramic, Ceramic to Metal Principal Use: Halogen Lamps
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.00 - 2.15 g/cc | 0.0723 - 0.0777 lb/in³ | |
| Volatile Organic Compounds (VOC) Content | 0.000 g/l | 0.000 g/l | |
| Viscosity | 40000 - 80000 cP | 40000 - 80000 cP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Impact Test | 36.6 J | 27.0 ft-lb | Torque Strength; curing at 1000°F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 6.84 µm/m-°C | 3.80 µin/in-°F | |
| Maximum Service Temperature, Air | 1650 °C | 3000 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 7.95 kV/mm | 202 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 50.0 - 90.0 °C | 122 - 194 °F | Application Temp |
| Cure Time | 120 min @Temperature 93.3 °C |
2.00 hour @Temperature 200 °F |
Step 1, preceeded by 1-4 hour air set |
| 120 min @Temperature 177 °C |
2.00 hour @Temperature 350 °F |
Step 2 | |
| 120 min @Temperature 260 °C |
2.00 hour @Temperature 500 °F |
Step 3 | |
| Shelf Life | 6.00 Month @Temperature 4.44 - 32.2 °C |
6.00 Month @Temperature 40.0 - 90.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Acid Resistance | Good | after curing at 700°F for 2 hours |
| Alkali Resistance | Excellent | after curing at 700°F for 2 hours |
| Color | White | |
| Mix Ratio | 100:60-80 | powder:liquid |
| Moisture Resistance | Good | after curing at 700°F for 2 hours |
| Solvent | Water | |
| Thinner | 835-MB-T |
Users viewing this material also viewed the following:
- Chevron Phillips 4516 Extrusion Coating Resin (discontinued **)
- Gouda Vuurvast B Dense Refractory Brick
- Solvay Specialty Polymers PrimoSpire® PR-250 Polyphenylene, Self-Reinforced (SRP)
- Vyncolit X655 Novolac Phenolic
- Asahi Glass Lumiflon FE-4500 Solvent Soluble Fluoropolymer
- Ametek P303L P/M Stainless Steel, Sintered from 6.7 g/cc Green Density
- Bayshore Vinyl Compounds BVC 1100-65 Clear PVC Compound
- Polimeri Europa EDISTIR PD RK6223N High Impact Polystyrene (HIPS) (discontinued **)
- Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled
- SABIC Innovative Plastics LNP STAT-KON ME003S PP (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved