Arkema Group Orgalloy® LE 60THM Flexible Nylon Alloy (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon, Flexible Alloy
Manufacturer Arkema
Trade Name Orgalloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Orgalloy® LE 60THM Flexible Nylon Alloy (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LE series, flexible polyamide alloys: processability on PE screw, low moisture absorption, chemical resistance (no known solvents).higher in rigidity than LE 6000. For film, hollow vessel blow molding and for injection molding.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.02 g/cc
0.0368 lb/in³
Water Absorption 6.0 %
6.0 %
Moisture Absorption at Equilibrium 1.8 %
1.8 %
Humidity Absorption
Melt Flow 3.0 g/10 min

@Load 2.16 kg,
Temperature 235 °C
3.0 g/10 min

@Load 4.76 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 40.0 MPa
5800 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Nominal Strain; 50 mm/min
Elongation at Yield 7.0 %
7.0 %
50 mm/min
Tensile Modulus 1.75 GPa
254 ksi
1 mm/min
Charpy Impact, Notched 1.25 J/cm²
5.95 ft-lb/in²
1.03 J/cm²

@Temperature -30.0 °C
4.90 ft-lb/in²

@Temperature -22.0 °F
Tensile Creep Modulus, 1 hour 1520 MPa
220000 psi
Tensile Creep Modulus, 1000 hours 690 MPa
100000 psi
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10°C/min
Deflection Temperature at 0.46 MPa (66 psi) 47.0 °C
117 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V