Arlon 43191R012 0.012" (0.305 mm) Uncured Silicone Rubber with Fiberglass Substrate

Category Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 43191R012 0.012" (0.305 mm) Uncured Silicone Rubber with Fiberglass Substrate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction:Side 1: Uncured Silicone Rubber Side 2: Uncured Silicone Rubber Appearance: Red silicone gum on fiberglass clothThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
Physical Properties Metric English Comments
Thickness 76.2 microns
3.00 mil
Polyethylene Interleave
76.2 - 102 microns
3.00 - 4.00 mil
Side 1
76.2 - 102 microns
3.00 - 4.00 mil
Side 2
102 microns
4.00 mil
Prime Coated 112 Fiberglass, Substrate
279 - 330 microns
11.0 - 13.0 mil
Overall
Mechanical Properties Metric English Comments
Hardness, Shore A 45 - 55
45 - 55
Compound Property
Tensile Strength >= 5.86 MPa
>= 850 psi
Compound Property
Elongation at Break >= 350 %
>= 350 %
Compound Property
Peel Strength >= 1.40 kN/m
>= 8.00 pli
Bond Strength
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 232 °C
450 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
Flammability Test <= 3.0
<= 3.0
[in], Char Length
<= 25
<= 25
[sec], Flame and Glow Time; FTMS 191A, Method 5903
Electrical Properties Metric English Comments
Dielectric Strength >= 15.7 kV/mm
>= 400 kV/in
Processing Properties Metric English Comments
Cure Time 120 min

@Temperature 204 °C
2.00 hour

@Temperature 400 °F
Recommended Postcure Cycle
15.0 min

@Pressure 0.345 MPa,
Temperature 177 °C
0.250 hour

@Pressure 50.0 psi,
Temperature 350 °F
Recommended Cure Cycle
Shelf Life 6.00 Month

@Temperature 21.1 °C
6.00 Month

@Temperature 70.0 °F
From date of manufacture
Descriptive Properties Value Comments
Color Red
Total Product Weight (oz/yd2) 10.3 - 12.3
Uncoated Fabric Break Strength 80 lb/in
Fill Direction, Substrate Property
90 lb/in
Warp Direction, Substrate Property