Ascend Performance Materials Vydyne® 67R Nylon 66, Heat Stabilized, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 67R Nylon 66, Heat Stabilized, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® 67R is a high-viscosity, heat-stabilized PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 67R resin offers high strength, rigidity and toughness over a broad range of demanding applications and good fluid resistance to a wide variety of chemicals, solvents and oils. Typical Applications/End Uses: Typical uses include packaging films, monofilaments, bristles, rods, tubing, sheet and extruded profiles.Availability:Asia PacificEuropeNorth America Additives: Heat Stabilizer Features: Gasoline ResistanceGeneral Purpose Good Chemical ResistanceGood ToughnessHeat StabilizedHigh Melt StabilityHigh RigidityHigh StrengthHigh ViscosityOil ResistantSolvent ResistantUses:Automotive ApplicationsFilmIndustrial ApplicationsMonofilamentsProfilesRodsSheetTubing Appearance: Natural ColorForms: PelletsProcessing Method: ExtrusionInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183
Water Absorption 8.5 %

@Time 86400 sec
8.5 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 2.5 %
2.5 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.022 cm/cm

@Diameter 2.00 mm
0.022 in/in

@Diameter 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.021 cm/cm

@Diameter 2.00 mm
0.021 in/in

@Diameter 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
ISO 527-2
Tensile Strength, Yield 85.0 MPa
12300 psi
ISO 527-2
Elongation at Break 40 %
40 %
ISO 527-2
Elongation at Yield 5.0 %
5.0 %
ISO 527-2
Tensile Modulus 2.85 GPa
413 ksi
ISO 527-2
Flexural Strength 80.0 MPa
11600 psi
ISO 178
Flexural Modulus 2.40 GPa
348 ksi
ISO 178
Poissons Ratio 0.40
0.40
ISO 527-2
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 180
7.00 kJ/m²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.700 J/cm²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-2
CTE, linear, Transverse to Flow 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-2
Melting Point 260 °C
500 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
Unannealed; ISO 75-2/A
Processing Properties Metric English Comments
Zone 1 250 - 295 °C
482 - 563 °F
Zone 2 250 - 295 °C
482 - 563 °F
Zone 3 250 - 295 °C
482 - 563 °F
Zone 4 250 - 295 °C
482 - 563 °F
Zone 5 250 - 295 °C
482 - 563 °F
Die Temperature 270 - 295 °C
518 - 563 °F
Melt Temperature 270 - 295 °C
518 - 563 °F
Roll Temperature 20.0 - 80.0 °C
68.0 - 176 °F
Chill Roll Remperature
Descriptive Properties Value Comments
Blow Film Bath Temperature 20-80°C
Melt Pressure 3-17 MPa