BASF Ultraform H 4320 Q600 POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer BASF
Trade Name Ultraform H
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultraform H 4320 Q600 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultraform H4320 Q600 is an extrusion POM high molecular weight grade. This grade enables high extrusion rates with thick-walled product. It also exhibits high thermal stability and a low tendency to discolor.
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
ISO 1183
Water Absorption 0.80 %
0.80 %
ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.; ISO 62
Melt Flow 26 g/10 min

@Load 2.16 kg,
Temperature 190 °C
26 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 125 MPa
18100 psi
358/30; ISO 2039-1
Tensile Strength, Yield 63.0 MPa
9140 psi
50mm/min; ISO 527
Elongation at Break 31 %
31 %
50mm/min; ISO 527
Elongation at Yield 10 %
10 %
50mm/min; ISO 527
Modulus of Elasticity 2.60 GPa
377 ksi
ISO 527
Izod Impact, Notched (ISO) 6.50 kJ/m²
3.09 ft-lb/in²
ISO 180/A
6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 180/A
Charpy Impact Unnotched 25.0 J/cm²
119 ft-lb/in²
ISO 179
18.0 J/cm²

@Temperature -30.0 °C
85.7 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
ISO 179
0.550 J/cm²

@Temperature -30.0 °C
2.62 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Tensile Creep Modulus, 1000 hours 1300 MPa
189000 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 12.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
6.67 µin/in-°F

@Temperature 73.4 - 131 °F
DIN 53752
Melting Point 166 °C
331 °F
DIN 53765
Maximum Service Temperature, Air 100 °C
212 °F
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
ISO 75
Vicat Softening Point 150 °C
302 °F
(50 °C/h / 50N) - B/50; ISO 306
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 3.8

@Frequency 100 Hz
3.8

@Frequency 100 Hz
IEC 60250
3.8

@Frequency 1.00e+6 Hz
3.8

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 40.0 kV/mm
1020 kV/in
IEC 60243-1
Dissipation Factor 0.0010

@Frequency 100 Hz
0.0010

@Frequency 100 Hz
IEC 60250
0.0050

@Frequency 1.00e+6 Hz
0.0050

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
600 V
600 V
Test Solution B; ICE 60112
Processing Properties Metric English Comments
Melt Temperature 190 - 230 °C
374 - 446 °F
Injection molding
Mold Temperature 60.0 - 120 °C
140 - 248 °F
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
FDA 21 CFR 177.1500
Form Pellets
Impact Modified No
NSF Std. 51 Yes
NSF Std. 61 Yes
Primary Processing Technique Extrusion
Processing Injection Molding
Other Extrusion
Profile Extrusion
Sheet Extrusion