BASF Ultramid® 8267G HS BK-102 15/25% Glass/Mineral Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8267G HS BK-102 15/25% Glass/Mineral Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8267G HS BK-102 is a heat stabilized, black pigmented, 40% mineral and glass fiber reinforced nylon 6 injection molding compound. It possesses a balance of engineering properties in combination with excellent dimensional stability, low warp and resistance to sink-mark formation. It exhibits high strength, rigidity, and good heat distortion temperature. It resists creep under load and the heat stabilizer system extends its retention of properties at elevated temperatures. It has good chemical resistance to greases, oils and hydrocarbons.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
ISO 1183
Water Absorption 0.90 %
0.90 %
24 hour; ISO Test
5.7 %
5.7 %
ISO 62
Moisture Absorption at Equilibrium 1.6 %
1.6 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM Test
Tensile Strength at Break 130 MPa
18900 psi
0.2 in/min; ASTM Test
Tensile Strength, Ultimate 125 MPa
18100 psi
5mm/min; ISO 527
Elongation at Break 3.0 %
3.0 %
5mm/min; ISO 527
3.0 %
3.0 %
0.2 in/min; ASTM Test
Tensile Modulus 8.30 GPa
1200 ksi
1mm/min; ISO 527
2.74 GPa

@Temperature 120 °C
397 ksi

@Temperature 248 °F
ISO Data
3.53 GPa

@Temperature 80.0 °C
512 ksi

@Temperature 176 °F
ISO Data
9.79 GPa

@Temperature -40.0 °C
1420 ksi

@Temperature -40.0 °F
ISO Data
Flexural Strength 195 MPa
28300 psi
ISO Data
215 MPa
31200 psi
ASTM Test
Flexural Modulus 7.20 GPa
1040 ksi
ISO Data
7.93 GPa
1150 ksi
ASTM Test
Izod Impact, Notched 0.550 J/cm

@Thickness 3.17 mm
1.03 ft-lb/in

@Thickness 0.125 in
ASTM Test
Izod Impact, Unnotched 7.40 J/cm
13.9 ft-lb/in
ASTM Test
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO Test
4.00 kJ/m²

@Temperature -40.0 °C
1.90 ft-lb/in²

@Temperature -40.0 °F
ISO Test
Charpy Impact Unnotched 5.20 J/cm²
24.7 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
ISO 179
0.350 J/cm²

@Temperature -30.0 °C
1.67 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear 31.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
17.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
CTE, linear, Parallel to Flow 30.0 µm/m-°C
16.7 µin/in-°F
ISO 11359
CTE, linear, Transverse to Flow 67.0 µm/m-°C
37.2 µin/in-°F
ISO 11359
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75
202 °C
396 °F
ASTM Test
Flammability, UL94 HB
HB
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Processing Properties Metric English Comments
Melt Temperature 275 °C
527 °F
Injection molding
Mold Temperature 95.0 °C
203 °F
Injection molding
Descriptive Properties Value Comments
Color BK-102
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat
UL.UL-C Yes