BASF Ultramid® A3W2G10 BK 20560 50% Glass Filled PA66 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® A3W2G10 BK 20560 50% Glass Filled PA66 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 50% glass fiber reinforced injection molding grade with optimized heat ageing performance for industrial articles having very high rigidity.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.500 - 0.800 g/cc
0.0181 - 0.0289 lb/in³
Density 1.55 g/cc
0.0560 lb/in³
ISO 1183
Water Absorption 3.7 - 4.3 %
3.7 - 4.3 %
ISO 62
Moisture Absorption at Equilibrium 1.0 - 1.4 %
1.0 - 1.4 %
ISO 62
Viscosity Measurement 140
140
ISO 307
Linear Mold Shrinkage 0.0035 cm/cm
0.0035 in/in
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 2577
Linear Mold Shrinkage, Transverse 0.0085 cm/cm
0.0085 in/in
ISO 2577
Melt Flow 15.5 g/10 min

@Load 5.00 kg,
Temperature 275 °C
15.5 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 255 MPa
37000 psi
ISO 527-1/-2
Elongation at Break 2.8 %
2.8 %
ISO 527-1/-2
Modulus of Elasticity 16.0 GPa
2320 ksi
ISO 527-1/-2
Charpy Impact Unnotched 10.0 J/cm²

@Temperature 23.0 °C
47.6 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
ISO 11357-1/-3
Maximum Service Temperature, Air 240 °C
464 °F
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ISO 527-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
ISO 527-1/-2
Decomposition Temperature >= 310 °C
>= 590 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 300 °C
572 °F
Feed zone
Zone 2 300 °C
572 °F
Compression
Zone 3 300 °C
572 °F
Metering-zone
Zone 4 300 °C
572 °F
Nozzle
Melt Temperature 280 - 310 °C
536 - 590 °F
Injection Molding/Extrusion
300 °C
572 °F
Optimal
Mold Temperature 80.0 °C
176 °F
Optimal
80.0 - 90.0 °C
176 - 194 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.030 - 0.060 %
0.030 - 0.060 %
Optimal
<= 0.15 %
<= 0.15 %
Descriptive Properties Value Comments
Color BK 20560
Commercial Status Europe
Ignition Temperature >400°C
ASTM D1929
Peripheral screw speed < 0.3 m/s