BASF Ultramid® KR 4357 G6 30% Glass Filled PA6/6T (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® KR 4357 G6 30% Glass Filled PA6/6T (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 30% glass-fiber reinforced, impact-modified product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties remain constant after moisture absorption up to a temperature of 60°C [140°F], for instance, for automotive plug-in connectors.Information provided by BASF
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Moisture Absorption at Equilibrium >= 0.80 %
>= 0.80 %
50% RH; ISO 62
>= 4.5 %
>= 4.5 %
Saturation; ISO 62
Mechanical Properties Metric English Comments
Tensile Strength at Break 165 MPa

@Temperature 23.0 °C
23900 psi

@Temperature 73.4 °F
ISO 527
249 MPa

@Temperature -40.0 °C
36100 psi

@Temperature -40.0 °F
ISO 527
Elongation at Break 3.5 %
3.5 %
ISO 527
Modulus of Elasticity 9.30 GPa
1350 ksi
ISO 527-1/-2
Izod Impact, Notched (ISO) 23.0 kJ/m²

@Temperature 23.0 °C
10.9 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Charpy Impact Unnotched 9.00 J/cm²

@Temperature -30.0 °C
42.8 ft-lb/in²

@Temperature -22.0 °F
ISO 179
9.50 J/cm²

@Temperature 23.0 °C
45.2 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179
1.90 J/cm²

@Temperature 23.0 °C
9.04 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
13.9 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 11359-1/-2
CTE, linear, Transverse to Flow 55.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
30.6 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 11359-1/-2
Specific Heat Capacity 1.40 J/g-°C
0.335 BTU/lb-°F
Melting Point 295 °C
563 °F
DIN 53765
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
ISO 75-1/-2
Decomposition Temperature >= 350 °C
>= 662 °F
UL RTI, Electrical 140 °C

@Thickness 1.50 mm
284 °F

@Thickness 0.0591 in
746B
UL RTI, Mechanical with Impact 110 °C

@Thickness 1.50 mm
230 °F

@Thickness 0.0591 in
746B
UL RTI, Mechanical without Impact 140 °C

@Thickness 1.50 mm
284 °F

@Thickness 0.0591 in
746B
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 4.3

@Frequency 1.00 Hz
4.3

@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.030

@Frequency 1.00e+6 Hz
0.030

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 300 °C
572 °F
Feed Zone
Zone 2 310 °C
590 °F
Compression
Zone 3 320 °C
608 °F
Metering-zone
Zone 4 320 °C
608 °F
Nozzle
Descriptive Properties Value Comments
Color BK 00564
Commercial Status North America
Peripheral screw speed <0.3 m/s