CLAL-MSX CUPROROR® TL5 Spring, Copper Alloy

Category Metal , Nonferrous Metal , Copper Alloy
Manufacturer CLAL-MSX
Trade Name CUPROROR®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF CLAL-MSX CUPROROR® TL5 Spring, Copper Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Alloy especially suited to applications in electronics and electro technology. This doped copper, displays high electrical and thermal conductivity, good mechanical properties and excellent temperature stability. CUPROFOR® is used in the manufacture of high power transistor supports, integrated circuits, electrical contacts and shunts.Applications: ElectronicsHeat sinks for power transistorsCUPROFOR® properties includeThermal conductivity to dissipate heatTemperature resistance permitting Pb/Sn soldering of the chip without loss of mechanical properties Mechanical strength to prevent deformation of heat dissipaters when moulding. CUPROFOR® can play an important part in the manufacture of power transistor heat sinks.For this application, CLAL offer 1/2 hard profile strips (condition TL2) in long length coils which can be delivered :totally or partially Ni coated, with an inlay of Pb/Sn, Ag or other material.Support media for printed circuitsThis application uses the following properties :temperature resistance, thus permitting the soldering of the integrated circuit of the DIE PAD, without loss of hardness in the support mediaOutstanding mechanical properties which guarantees the mechanical strength of the LEADSA high deformation capacity gives suitability to form external LEADS.For this application, CLAL, upon request offer long length tapes : a high standard of geometrical and dimensional accuracya stress relieving treatment to maintain that the LEADS TIPS are coplanar about the DIE PAD.The electro-technical fieldElectrical contactsContact mountsPushbuttonsConductive partsElectrical connections and terminals.Other fieldsHeat exchangersSeals and washersDephasing rings.Information provided by CLAL-MSX
Physical Properties Metric English Comments
Density 8.90 g/cc
0.322 lb/in³
Mechanical Properties Metric English Comments
Hardness, Vickers >= 150
>= 150
90

@Temperature 500 °C,
Time 1800 sec
90

@Temperature 932 °F,
Time 0.500 hour
Isotherm
129

@Temperature 500 °C,
Time 600 sec
129

@Temperature 932 °F,
Time 0.167 hour
Isotherm
132

@Temperature 500 °C,
Time 180 sec
132

@Temperature 932 °F,
Time 0.0500 hour
Isotherm
132

@Temperature 350 °C,
Time 1800 sec
132

@Temperature 662 °F,
Time 0.500 hour
Isotherm
134

@Temperature 350 °C,
Time 600 sec
134

@Temperature 662 °F,
Time 0.167 hour
Isotherm
134

@Temperature 350 °C,
Time 180 sec
134

@Temperature 662 °F,
Time 0.0500 hour
Isotherm
135

@Temperature 350 °C,
Time 60.0 sec
135

@Temperature 662 °F,
Time 0.0167 hour
Isotherm
138

@Temperature 500 °C,
Time 60.0 sec
138

@Temperature 932 °F,
Time 0.0167 hour
Isotherm
144

@Temperature 350 °C,
Time 30.0 sec
144

@Temperature 662 °F,
Time 0.00833 hour
Isotherm
145

@Temperature 500 °C,
Time 30.0 sec
145

@Temperature 932 °F,
Time 0.00833 hour
Isotherm
150

@Temperature 500 °C,
Time 10.0 sec
150

@Temperature 932 °F,
Time 0.00278 hour
Isotherm
151

@Temperature 350 °C,
Time 10.0 sec
151

@Temperature 662 °F,
Time 0.00278 hour
Isotherm
155

@Temperature 350 °C,
Time 0.000 sec
155

@Temperature 662 °F,
Time 0.000 hour
Isotherm
155

@Temperature 500 °C,
Time 0.000 sec
155

@Temperature 932 °F,
Time 0.000 hour
Isotherm
Tensile Strength, Ultimate >= 500 MPa
>= 72500 psi
Tensile Strength, Yield >= 450 MPa

@Strain 0.200 %
>= 65300 psi

@Strain 0.200 %
Elongation at Break 2.0 %
2.0 %
L<sub>O</sub>=5.65vS<sub>O</sub>
Modulus of Elasticity 140 GPa
20300 ksi
Flexural Strength 260 MPa
37700 psi
Elastic Limit in Bending, direction of rolling
310 MPa
45000 psi
Elastic Limit in Bending, across direction of rolling
Fatigue Strength 240 MPa
34800 psi
rotational bending
Thermal Properties Metric English Comments
CTE, linear 16.3 µm/m-°C

@Temperature 0.000 - 500 °C
9.06 µin/in-°F

@Temperature 32.0 - 932 °F
16.4 µm/m-°C

@Temperature 0.000 - 250 °C
9.11 µin/in-°F

@Temperature 32.0 - 482 °F
16.7 µm/m-°C

@Temperature 0.000 - 100 °C
9.28 µin/in-°F

@Temperature 32.0 - 212 °F
Specific Heat Capacity 0.383 J/g-°C
0.0915 BTU/lb-°F
Thermal Conductivity 338 W/m-K
2350 BTU-in/hr-ft²-°F
Melting Point 1080 °C
1980 °F
Component Elements Properties Metric English Comments
Cobalt, Co 0.080 %
0.080 %
Phosphorous, P 0.080 %
0.080 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000181 - 0.00000229 ohm-cm
0.00000181 - 0.00000229 ohm-cm