Chevron Phillips 6335B LLDPE Cast/Blown Film Resin, Butene Copolymer  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips 6335B LLDPE Cast/Blown Film Resin, Butene Copolymer  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resin Type: Butene Copolymer, Medium Slip Version of 6335Characteristics: Good Optics, Good Drawdown, Can be used straight or blended with LDPE or HDPE, Can be used in blown or cast applications, Low COF. Slip 1000 ppm.Applications:Bakery Films, CoextrusionsProcessing Conditions: Extruder 6.35 cm. Screw L/D Ratio 24:1. Die Opening 0.1016 cm.Film properties below based on film thickness of 31.8 µm.Data provided by Chevron Chemical.
Physical Properties Metric English Comments
Density 0.925 g/cc
0.0334 lb/in³
ASTM D1505
Melt Flow 3.5 g/10 min
3.5 g/10 min
Condition E; ASTM D 1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 520 %
520 %
ASTM D882
Film Elongation at Break, TD 740 %
740 %
ASTM D882
Secant Modulus, MD 0.200 GPa
29.0 ksi
ASTM D882
Secant Modulus, TD 0.220 GPa
31.9 ksi
ASTM D882
Coefficient of Friction <= 0.10
<= 0.10
ASTM D1894
Elmendorf Tear Strength, MD 2.36 g/micron
60.0 g/mil
Notched; ASTM D1922
Elmendorf Tear Strength, TD 15.0 g/micron
380 g/mil
ASTM D1922
Dart Drop 1.90 g/micron
48.3 g/mil
F<sub>50</sub>; 1.5 in. dart/26 in. drop height; ASTM D 1709
Film Tensile Strength at Break, MD 32.0 MPa
4640 psi
ASTM D882
Film Tensile Strength at Break, TD 32.0 MPa
4640 psi
ASTM D882
Optical Properties Metric English Comments
Haze 4.0 %
4.0 %
ASTM D2457
Gloss 90 %
90 %
at 45°. ASTM D 2457
140 %
140 %
at 60°. ASTM D 2457
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F