Chevron Phillips Xtel® XK2760BL Polyphenylene Sulfide Alloy  (discontinued **)

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips Xtel® XK2760BL Polyphenylene Sulfide Alloy  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Xtel® XK2760BL is a high performance, glass fiber and mineral filled PPS based alloy developed to provide excellent mechanical strength with a unique blend of toughness, rigidity, and low flash characteristics.Information provided by Chevron PhillipsMeasured on 102mm x 102mm x 3.2 mm plaques, edge gated.
Physical Properties Metric English Comments
Density 1.80 g/cc
0.0650 lb/in³
ISO 1183A
Water Absorption 0.20 %
0.20 %
ASTM D-570
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
Mechanical Properties Metric English Comments
Tensile Strength, Yield 165 MPa
23900 psi
ISO 527
Elongation at Yield 1.3 %
1.3 %
ISO 527
Flexural Strength 240 MPa
34800 psi
ISO 178
Flexural Modulus 16.0 GPa
2320 ksi
ISO 178
Compressive Strength 240 MPa
34800 psi
ISO 604
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
ISO 180A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²
11.9 ft-lb/in²
ISO 180A
Thermal Properties Metric English Comments
CTE, linear 10.0 µm/m-°C

@Temperature 100 - 200 °C
5.56 µin/in-°F

@Temperature 212 - 392 °F
Axial; ISO 11359-2
15.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
8.33 µin/in-°F

@Temperature -58.0 - 122 °F
Axial; ISO 11359-2
CTE, linear, Transverse to Flow 40.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
22.2 µin/in-°F

@Temperature -58.0 - 122 °F
ISO 11359-2
95.0 µm/m-°C

@Temperature 100 - 200 °C
52.8 µin/in-°F

@Temperature 212 - 392 °F
ISO 11359-2
Thermal Conductivity 0.530 W/m-K
3.68 BTU-in/hr-ft²-°F
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
ISO 75
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
ASTM D-257
Insulation Resistance 1.00e+12 ohm

@Temperature 90.0 °C,
Time 173000 sec
1.00e+12 ohm

@Temperature 194 °F,
Time 48.0 hour
95% RH
Dielectric Constant 5.0

@Frequency 1000 Hz
5.0

@Frequency 1000 Hz
ASTM D-150
5.0

@Frequency 1e+6 Hz
5.0

@Frequency 1e+6 Hz
ASTM D-150
Dielectric Strength 20.0 kV/mm
508 kV/in
ASTM D-149
Dissipation Factor 0.015

@Frequency 1000 Hz
0.015

@Frequency 1000 Hz
ASTM D-150
0.015

@Frequency 1e+6 Hz
0.015

@Frequency 1e+6 Hz
ASTM D-150
Arc Resistance 130 sec
130 sec
ASTM D-495
Comparative Tracking Index 275 V
275 V
UL 746A
Processing Properties Metric English Comments
Melt Temperature 280 - 305 °C
536 - 581 °F
Mold Temperature 100 °C
212 °F