DuPont Performance Polymers Sorona® MT3401 NC010 Polytrimethylene Terephthalate (PTT)

Category Polymer , Thermoplastic , Polyester, TP , Polytrimethylene Terephthalate (PTT)
Manufacturer DuPont Performance Polymers
Trade Name Sorona®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Sorona® MT3401 NC010 Polytrimethylene Terephthalate (PTT).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced Renewably Sourced Polytrimethylene Terephthalate with Excellent Impact Resistance Sorona MT3401 NC010 is a medium toughened polytrimethylene terephthalate resin containing 29% renewably sourced ingredients by weight. It was initially codedInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
1.23 g/cc
0.0444 lb/in³
ISO 1183
Water Absorption 0.34 %

@Thickness 2.00 mm
0.34 %

@Thickness 0.0787 in
Sim. to ISO 62
Moisture Absorption 0.110 %

@Thickness 2.00 mm
0.110 %

@Thickness 0.0787 in
Sim. to ISO 62
Water Absorption at Saturation 0.080 %
0.080 %
Immersion 24h; ASTM D570
Viscosity 70540 cP

@Shear Rate 5000 1/s,
Temperature 270 °C
70540 cP

@Shear Rate 5000 1/s,
Temperature 518 °F
ISO 11403-1 -2
75970 cP

@Shear Rate 5000 1/s,
Temperature 260 °C
75970 cP

@Shear Rate 5000 1/s,
Temperature 500 °F
ISO 11403-1 -2
82100 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
82100 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
ISO 11403-1 -2
277400 cP

@Shear Rate 500 1/s,
Temperature 270 °C
277400 cP

@Shear Rate 500 1/s,
Temperature 518 °F
ISO 11403-1 -2
312300 cP

@Shear Rate 500 1/s,
Temperature 260 °C
312300 cP

@Shear Rate 500 1/s,
Temperature 500 °F
ISO 11403-1 -2
351600 cP

@Shear Rate 500 1/s,
Temperature 250 °C
351600 cP

@Shear Rate 500 1/s,
Temperature 482 °F
ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.015 cm/cm
0.015 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.017 cm/cm
0.017 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength, Yield 35.0 MPa
5080 psi
ISO 527-1/-2
Elongation at Break 15 %
15 %
Nominal; ISO 527-1/-2
Elongation at Yield 5.0 %
5.0 %
ISO 527-1/-2
Tensile Modulus 1.60 GPa
232 ksi
ISO 527-1/-2
Flexural Modulus 1.60 GPa
232 ksi
ISO 178
Izod Impact, Notched (ISO) 18.0 kJ/m²
8.57 ft-lb/in²
ISO 180/1A
Charpy Impact, Notched 2.20 J/cm²
10.5 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 138 µm/m-°C
76.7 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 138 µm/m-°C
76.7 µin/in-°F
ISO 11359-1/-2
Specific Heat Capacity 2.10 J/g-°C
0.502 BTU/lb-°F
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
of melt
Melting Point 229 °C
444 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 75.0 °C
167 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 53.0 °C
127 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
IEC 60695-11-10
HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance 6.00e+14 ohm
6.00e+14 ohm
IEC 60093
Dielectric Constant 3.4

@Frequency 1.00e+6 Hz
3.4

@Frequency 1.00e+6 Hz
IEC 60250
3.6

@Frequency 100 Hz
3.6

@Frequency 100 Hz
IEC 60250
Dielectric Strength 32.0 kV/mm
813 kV/in
IEC 60243-1
Dissipation Factor 0.0020

@Frequency 100 Hz
0.0020

@Frequency 100 Hz
IEC 60250
0.0205

@Frequency 1.00e+6 Hz
0.0205

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Additives Release agent
Delivery Form Pellets
Part Marking Code >PTT-I<
ISO 11469
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification PTT-I