Ensinger TECASINT 3062 Polyimide, Shiny Black, 15% Graphite, 10% PTFE (PI)

Category Polymer , Thermoplastic , Polyimide, Thermoplastic , Thermoplastic Polyimide, Graphite Filled , Thermoplastic Polyimide, Molded, PTFE Filled
Manufacturer Ensinger
Trade Name TECASINT
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ensinger TECASINT 3062 Polyimide, Shiny Black, 15% Graphite, 10% PTFE (PI).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excellent wear resistance among other things. The TECASINT 2000 series offers these enhanced thermal properties along with lower moisture absorption, a higher degree of toughness, and better machining properties. TECASINT 2011 is unfilled, while TECASINT 2021 contains 15% graphite which offer improved wear resistance and a lower coefficient of friction. TECASINT 2000 series with their superior physical properties, are ideal for application in the aerospace, nuclear, automotive, electrical/electronics, and chemical processing industries.Main features: High thermal and mechanical capacity, very creep resistant, broad chemical compatibility, good sliding properties, low water absorption, no electrical insulation, flame retardant according to UL94 V-0, sensitive to hydrolysis in higher thermal range, low static frictionApplications: Mechanical engineering, automotive industry, materials handling equipment, precision engineering, aircraft and aerospace industries, textile industryPreferred Fields: Valve seating, chain guides, piston rings, sliding rails, thrust washers, bearings, bushingsInformation Provided by Ensinger Sintimid
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
DIN 53 479
Water Absorption 0.43 %

@Temperature 23.0 °C
0.43 %

@Temperature 73.4 °F
24 hours in water; EN ISO 62
1.7 %

@Temperature 80.0 °C
1.7 %

@Temperature 176 °F
24 hours in water; EN ISO 62
Mechanical Properties Metric English Comments
Hardness, Shore D 78

@Temperature 23.0 °C
78

@Temperature 73.4 °F
DIN 53 505
Tensile Strength 44.1 MPa

@Temperature 23.0 °C
6400 psi

@Temperature 73.4 °F
EN ISO 527
Elongation at Break 3.6 %

@Temperature 23.0 °C
3.6 %

@Temperature 73.4 °F
EN ISO 527
Elongation at Yield 3.3 %

@Temperature 23.0 °C
3.3 %

@Temperature 73.4 °F
Flexural Elongation; EN ISO 178
Tensile Modulus 2.646 GPa

@Temperature 23.0 °C
383.8 ksi

@Temperature 73.4 °F
EN ISO 527
Flexural Strength 62.0 MPa

@Temperature 23.0 °C
8990 psi

@Temperature 73.4 °F
EN ISO 178
Flexural Modulus 2.74 GPa

@Temperature 23.0 °C
397 ksi

@Temperature 73.4 °F
EN ISO 178
Compressive Yield Strength 70.0 MPa

@Strain 10.0 %,
Temperature 23.0 °C
10200 psi

@Strain 10.0 %,
Temperature 73.4 °F
EN ISO 604
Compressive Strength 180 MPa

@Temperature 23.0 °C
26100 psi

@Temperature 73.4 °F
EN ISO 604
Compressive Modulus 0.847 GPa

@Temperature 23.0 °C
123 ksi

@Temperature 73.4 °F
EN ISO 604
Charpy Impact Unnotched 1.78 J/cm²

@Temperature 23.0 °C
8.47 ft-lb/in²

@Temperature 73.4 °F
EN ISO 179
Charpy Impact, Notched 0.420 J/cm²

@Temperature 23.0 °C
2.00 ft-lb/in²

@Temperature 73.4 °F
EN ISO 179
Compression Set 48 %

@Temperature 23.0 °C
48 %

@Temperature 73.4 °F
Compression at Break; EN ISO 604
Thermal Properties Metric English Comments
CTE, linear 45.0 µm/m-°C

@Temperature 50.0 - 200 °C
25.0 µin/in-°F

@Temperature 122 - 392 °F
DIN 53 752
57.0 µm/m-°C

@Temperature 200 - 300 °C
31.7 µin/in-°F

@Temperature 392 - 572 °F
DIN 53 752