ExxonMobil LDPE LD 313.NF Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Exxon Chemical
Trade Name LDPE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LDPE LD 313.NF Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LD 313.NF is a 3 % vinyl acetate copolymer. The vinyl acetate content of this resin provides good heat sealing and good cold temperature toughness when compared to LDPE homopolymers.Availability: Latin America, North America and South America Additive: Antiblock: 2500 ppmSlip: 800 ppm Thermal Stabilizer: YesApplications: Carpet BackingCoextrusion FilmsFoamsForm Fill and Seal PackagingFreezer FilmHigh Clarity FilmLamination Film Information provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.925 g/cc
0.0334 lb/in³
ExxonMobil method
Vinyl Acetate Content 3.0 %
3.0 %
ExxonMobil Method
Melt Flow 2.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 2500 ppm
2500 ppm
Slip Level 800 ppm
800 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.27 MPa
1200 psi
ASTM D882
Film Tensile Strength at Yield, TD 8.27 MPa
1200 psi
ASTM D882
Film Elongation at Break, MD 170 %
170 %
ASTM D882
Film Elongation at Break, TD 540 %
540 %
ASTM D882
Puncture Energy 0.350 J
0.258 ft-lb
ExxonMobil Method
Elmendorf Tear Strength MD 200 g
200 g
ASTM D1922
Elmendorf Tear Strength TD 120 g
120 g
ASTM D1922
Dart Drop Test 120 g
0.265 lb
ASTM D1709A
Film Tensile Strength at Break, MD 22.1 MPa
3200 psi
ASTM D882
Film Tensile Strength at Break, TD 19.3 MPa
2800 psi
ASTM D882
1% Secant Modulus, MD 152 MPa
22000 psi
ASTM D882
1% Secant Modulus, TD 179 MPa
26000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 225 °C
<= 437 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 5.3 %
5.3 %
ASTM D1003
Gloss 76 %
76 %
45°; ASTM D2457
Descriptive Properties Value Comments
Puncture Force 6 lbf
ExxonMobil Method