ExxonMobil Pax-Plus™ 3201 Blown Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer Exxon Chemical
Trade Name Pax-Plus™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Pax-Plus™ 3201 Blown Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Pax-Plus 3201 is a rubber modified high density polyethylene film resin that exhibits excellent impact strength and stress crack resistance. It is used primarily in film where its good tear resistance and laminating properties are required.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.936 g/cc
0.0338 lb/in³
ExxonMobil Method
Thickness 50.8 microns
2.00 mil
Melt Flow 0.20 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.20 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ExxonMobil Method
4.0 g/10 min

@Load 10.0 kg,
Temperature 190 °C
4.0 g/10 min

@Load 22.0 lb,
Temperature 374 °F
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.6 MPa
1680 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 12.1 MPa
1750 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 700 %
700 %
ASTM D882
Film Elongation at Break, TD 900 %
900 %
ASTM D882
Elmendorf Tear Strength MD 70 g
70 g
ASTM D1922
Elmendorf Tear Strength TD 770 g
770 g
ASTM D1922
Elmendorf Tear Strength, MD 1.38 g/micron
35.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 15.2 g/micron
385 g/mil
ASTM D1922
Dart Drop 6.30 g/micron
160 g/mil
ASTM D1709
Dart Drop Test 320 g
0.706 lb
ASTM D1709
Film Tensile Strength at Break, MD 26.8 MPa
3880 psi
ASTM D882
Film Tensile Strength at Break, TD 23.1 MPa
3350 psi
ASTM D882
1% Secant Modulus, MD 325 MPa
47100 psi
ASTM D882
1% Secant Modulus, TD 387 MPa
56200 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 130 °C
266 °F
Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point 105 °C
221 °F
ExxonMobil Method
Descriptive Properties Value Comments
Features Thermal Stabilizer