Iran Petrochemical (PCC) HIPS 8350 High Impact Polystyrene

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer Iran Petrochemical Commercial Co. (PCC)
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Iran Petrochemical (PCC) HIPS 8350 High Impact Polystyrene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
HIPS 8350 is a very high impact polystyrene used in the extrusion industry. This grade has an improved environmental stress crack resistance (ESCR) in comparison with standard high impact polystyrene grades. It is recommended for the production of packaging intended for products likely to cause stress cracking. HIPS8350 retains good mechanical properties at low temperatures making this grade suitable for frozen food packaging and for the production of fridge liners in contact with HCFC expanded foam insulation.Applications: extrusion sheet for thermoforming, fridge doors and cabinet linersInformation provided by Iran Petrochemical Commercial Co.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
Moisture Absorption <= 0.100 %
<= 0.100 %
ASTM D570
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D570
Melt Flow 4.5 g/10 min

@Load 5.00 kg,
Temperature 200 °C
4.5 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 20.0 MPa
2900 psi
ASTM D638
Tensile Strength, Yield 18.0 MPa
2610 psi
ASTM D638
Elongation at Break 60 %
60 %
ASTM D638
Tensile Modulus 1.60 GPa
232 ksi
ASTM D638
Flexural Modulus 1.60 GPa
232 ksi
ASTM D790
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
ISO 180/1A
Thermal Properties Metric English Comments
Vicat Softening Point >= 92.0 °C
>= 198 °F
ASTM D1525