LATI Latilub 80-10T G/40 PPS, 40% Glass Fiber Reinforced, PTFE Filled

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), PTFE/Glass-Fiber Filled
Manufacturer LATI
Trade Name Latilub
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 80-10T G/40 PPS, 40% Glass Fiber Reinforced, PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyphenylene Sulfide (PPS). PTFE. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.72 g/cc
0.0621 lb/in³
Linear Mold Shrinkage, Flow 0.0010 - 0.0025 cm/cm
0.0010 - 0.0025 in/in
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 160 MPa
23200 psi
Elongation at Break 1.5 %
1.5 %
Tensile Modulus 14.5 GPa
2100 ksi
Charpy Impact Unnotched 4.50 J/cm²
21.4 ft-lb/in²
Charpy Impact, Notched 0.850 J/cm²
4.04 ft-lb/in²
Coefficient of Friction, Dynamic 0.23
0.23
Coefficient of Friction, Static 0.26
0.26
K (wear) Factor 10.0 x 10-8 mm³/N-M
4.96 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 280 °C
536 °F
Deflection Temperature at 1.8 MPa (264 psi) 265 °C
509 °F
Vicat Softening Point 260 °C

@Load 5.00 kg
500 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 290 - 310 °C
554 - 590 °F
Mold Temperature 130 - 150 °C
266 - 302 °F
Drying Temperature 130 - 150 °C

@Time 10800 sec
266 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa
Copyright © lookpolymers.com All Rights Reserved