LNP Thermocomp® JF-1006 Polyethersulfone, Glass Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Thermocomp® JF-1006 Polyethersulfone, Glass Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.58 g/cc
1.58 g/cc
Method A; ASTM D792
Water Absorption 0.30 %
0.30 %
at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 143 MPa
20700 psi
ASTM D638
Tensile Strength, Yield 143 MPa
20700 psi
ASTM D638
Elongation at Break 2.2 %
2.2 %
ASTM D638
Elongation at Yield 2.2 %
2.2 %
ASTM D638
Tensile Modulus 10.8 GPa
1570 ksi
ASTM D638
Flexural Strength 207 MPa
30000 psi
ASTM D790
Flexural Modulus 9.72 GPa
1410 ksi
ASTM D790
Izod Impact, Notched (ISO) 9.50 kJ/m²
4.52 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 40.0 kJ/m²
19.0 ft-lb/in²
ISO 180
Falling Dart Impact 10.7 J
7.89 ft-lb
ASTM D3763
Impact Test 4.16 J
3.07 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Coefficient of Friction, Dynamic 0.52
0.52
vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894
Coefficient of Friction, Static 0.57
0.57
vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894
K (wear) Factor 342 x 10-8 mm³/N-M
170 x 10-10 in³-min/ft-lb-hr
40psi, 50ft/min; tested in accordance with LNP WI-0687
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 354 - 371 °C
669 - 700 °F
Mold Temperature 135 - 149 °C
275 - 300 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.050 %
0.050 %
Suggested
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi