Lanxess Durethan® A 30 H2.0 901510 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® A 30 H2.0 901510 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66 standard injection molding grade, non-reinforced, very easy release, good heat-ageing resistanceApplication Examples: terminal blocks, cable clips, bobbins, gearwheels
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption | 8.0 % | 8.0 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 2.6 % | 2.6 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 144 cm³/g | 144 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Melt Flow | 148 g/10 min @Load 5.00 kg, Temperature 280 °C |
148 g/10 min @Load 11.0 lb, Temperature 536 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Conditioned; ISO 527-1/-2 |
| 90.0 MPa | 13100 psi | ISO 527-1/-2 | |
| Elongation at Break | >= 50 % | >= 50 % | Nominal, Conditioned; ISO 527-1/-2 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1/-2 |
| 15 % | 15 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 1.50 GPa | 218 ksi | Conditioned; ISO 527-1/-2 |
| 3.50 GPa | 508 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 9.00 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 3900 | 3900 | Puncture maximum force (N); ISO 6603-2 |
| 4641 | 4641 | Puncture maximum force, Conditioned (N); ISO 6603-2 | |
| 3170 @Temperature -30.0 °C |
3170 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 20.0 J | 14.8 ft-lb | ISO 6603-2 |
| 28.0 J | 20.7 ft-lb | Conditioned; ISO 6603-2 | |
| 8.20 J @Temperature -30.0 °C |
6.05 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 8.20 J @Temperature -30.0 °C |
6.05 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 | |
| Tensile Creep Modulus, 1 hour | 1000 MPa | 145000 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 700 MPa | 102000 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 263 °C | 505 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 50.0 °C | 122 °F | ISO 75-1/-2 |
| Vicat Softening Point | 230 °C | 446 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
IEC 60695-11-10 |
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
IEC 60695-11-10 | |
| Oxygen Index | 24 % | 24 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 60250 | |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 12 @Frequency 100 Hz |
12 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | Conditioned; IEC 60243-1 |
| 29.0 kV/mm | 737 kV/in | IEC 60243-1 | |
| Dissipation Factor | 0.0060 @Frequency 100 Hz |
0.0060 @Frequency 100 Hz |
IEC 60250 |
| 0.018 @Frequency 1.00e+6 Hz |
0.018 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.090 @Frequency 1.00e+6 Hz |
0.090 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.32 @Frequency 100 Hz |
0.32 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 575 V | 575 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Lubricants | |
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 66,MHR,14-030 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Potters Industries Conduct-O-Fil® SN325P25-LD Silver-coated Nickel Granules
- ITW Devcon Metal Repair Ceramic Repair Putty, Dark Blue
- LATI Lasulf G/30 PSU, 30% Glass Fiber Reinforced
- Styrolution Terluran® HI-10 ABS
- Borealis RJ470MO Polypropylene, Transparent Random Copolymer
- A. Schulman POLYBATCH™ White HS8350 Concentrate Based In Impact Polystyrene
- Dow SiLK™ I 360 Semiconductor Dielectric Resin
- Compuestos Dominicanos Polycom BF-314699 PVC Compound
- Axiall SP-6340 Rigid PVC, Molding
Copyright © lookpolymers.com All Rights Reserved