Overview of materials for Acrylonitrile Butadiene Styrene (ABS), PTFE Filled

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), PTFE Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Acrylonitrile Butadiene Styrene (ABS), PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), PTFE Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.05 - 1.32 g/cc
0.0379 - 0.0477 lb/in³
Average value: 1.12 g/cc Grade Count:11
Filler Content 5.00 - 20.0 %
5.00 - 20.0 %
Average value: 11.7 % Grade Count:6
Water Absorption 0.190 - 0.300 %
0.190 - 0.300 %
Average value: 0.233 % Grade Count:4
Linear Mold Shrinkage 0.00400 - 0.00700 cm/cm
0.00400 - 0.00700 in/in
Average value: 0.00577 cm/cm Grade Count:11
Melt Flow 4.50 - 8.20 g/10 min
4.50 - 8.20 g/10 min
Average value: 5.73 g/10 min Grade Count:3
Mechanical Properties Metric English Comments
Hardness, Rockwell R 96.0 - 103
96.0 - 103
Average value: 101 Grade Count:4
Tensile Strength, Ultimate 34.5 - 44.8 MPa
5000 - 6500 psi
Average value: 39.5 MPa Grade Count:10
Tensile Strength, Yield 27.6 - 47.6 MPa
4000 - 6900 psi
Average value: 35.2 MPa Grade Count:3
Elongation at Break 2.00 - 15.0 %
2.00 - 15.0 %
Average value: 9.00 % Grade Count:11
Modulus of Elasticity 2.21 - 2.76 GPa
320 - 400 ksi
Average value: 2.46 GPa Grade Count:8
Flexural Yield Strength 41.0 - 75.8 MPa
5950 - 11000 psi
Average value: 64.8 MPa Grade Count:12
Flexural Modulus 2.07 - 2.76 GPa
300 - 400 ksi
Average value: 2.40 GPa Grade Count:12
Izod Impact, Notched 0.427 - 2.67 J/cm
0.800 - 5.00 ft-lb/in
Average value: 1.25 J/cm Grade Count:12
0.5339 - 1.01441 J/cm

@Temperature -40.0 - 0.000 °C
1.000 - 1.90041 ft-lb/in

@Temperature -40.0 - 32.0 °F
Average value: 0.774 J/cm Grade Count:2
0.5339 - 1.01441 J/cm

@Thickness 3.17 - 3.17 mm
1.000 - 1.90041 ft-lb/in

@Thickness 0.125 - 0.125 in
Average value: 0.774 J/cm Grade Count:2
Izod Impact, Unnotched 3.74 - 8.01 J/cm
7.00 - 15.0 ft-lb/in
Average value: 5.49 J/cm Grade Count:7
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 98.9 - 104 °C
210 - 219 °F
Average value: 101 °C Grade Count:5
Deflection Temperature at 1.8 MPa (264 psi) 77.8 - 98.9 °C
172 - 210 °F
Average value: 90.6 °C Grade Count:10
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:7
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+14 - 1.00e+17 ohm-cm
1.00e+14 - 1.00e+17 ohm-cm
Average value: 2.55e+16 ohm-cm Grade Count:4
Processing Properties Metric English Comments
Melt Temperature 177 - 260 °C
351 - 500 °F
Average value: 221 °C Grade Count:9
Mold Temperature 48.9 - 85.0 °C
120 - 185 °F
Average value: 70.5 °C Grade Count:9
Drying Temperature 60.0 - 93.3 °C
140 - 200 °F
Average value: 81.0 °C Grade Count:9
Moisture Content 0.0100 - 0.100 %
0.0100 - 0.100 %
Average value: 0.0856 % Grade Count:8
Dew Point -17.8 °C
0.000 °F
Average value: -17.8 °C Grade Count:6
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Average value: 86.2 MPa Grade Count:6