Overview of materials for Polypropylene, Carbon Fiber Filled

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polypropylene, Carbon Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Carbon Fiber 10%". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.872 - 1.23 g/cc
0.0315 - 0.0444 lb/in³
Average value: 1.02 g/cc Grade Count:19
Filler Content 1.00 - 50.0 %
1.00 - 50.0 %
Average value: 19.7 % Grade Count:14
Water Absorption 0.0100 %
0.0100 %
Average value: 0.0100 % Grade Count:7
Linear Mold Shrinkage 0.000500 - 0.0100 cm/cm
0.000500 - 0.0100 in/in
Average value: 0.00311 cm/cm Grade Count:14
Melt Flow 1.10 - 9.80 g/10 min
1.10 - 9.80 g/10 min
Average value: 4.93 g/10 min Grade Count:4
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 19.3 - 117 MPa
2800 - 17000 psi
Average value: 45.5 MPa Grade Count:20
Elongation at Break 0.400 - 436 %
0.400 - 436 %
Average value: 34.4 % Grade Count:22
Modulus of Elasticity 1.03 - 27.6 GPa
150 - 4000 ksi
Average value: 9.05 GPa Grade Count:20
Flexural Yield Strength 31.0 - 186 MPa
4500 - 27000 psi
Average value: 75.4 MPa Grade Count:18
Flexural Modulus 2.76 - 19.3 GPa
400 - 2800 ksi
Average value: 8.51 GPa Grade Count:18
Izod Impact, Notched 0.427 - 3.20 J/cm
0.800 - 6.00 ft-lb/in
Average value: 1.14 J/cm Grade Count:16
Izod Impact, Unnotched 1.07 - 11.2 J/cm
2.00 - 21.0 ft-lb/in
Average value: 3.74 J/cm Grade Count:17
Charpy Impact, Notched 0.240 - 0.320 J/cm²
1.14 - 1.52 ft-lb/in²
Average value: 0.290 J/cm² Grade Count:4
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
Average value: 165 °C Grade Count:5
Deflection Temperature at 0.46 MPa (66 psi) 132 - 166 °C
270 - 330 °F
Average value: 143 °C Grade Count:5
Deflection Temperature at 1.8 MPa (264 psi) 104 - 149 °C
220 - 300 °F
Average value: 130 °C Grade Count:11
Flammability, UL94 HB
HB
Grade Count:7
Electrical Properties Metric English Comments
Electrical Resistivity 1.00 - 3.10e+9 ohm-cm
1.00 - 3.10e+9 ohm-cm
Average value: 2.40e+8 ohm-cm Grade Count:16
Surface Resistance 100 - 1.10e+11 ohm
100 - 1.10e+11 ohm
Average value: 1.56e+10 ohm Grade Count:12
Static Decay 0.100 - 2.00 sec
0.100 - 2.00 sec
Average value: 1.51 sec Grade Count:7
Processing Properties Metric English Comments
Processing Temperature 188 - 227 °C
370 - 440 °F
Average value: 209 °C Grade Count:8
Nozzle Temperature 204 - 216 °C
400 - 420 °F
Average value: 210 °C Grade Count:3
Melt Temperature 191 - 250 °C
375 - 482 °F
Average value: 214 °C Grade Count:9
Mold Temperature 30.0 - 79.4 °C
86.0 - 175 °F
Average value: 53.5 °C Grade Count:17
Injection Velocity 50.8 - 76.2 mm/sec
2.00 - 3.00 in/sec
Average value: 63.5 mm/sec Grade Count:3
Drying Temperature 70.0 - 79.4 °C
158 - 175 °F
Average value: 77.9 °C Grade Count:6
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Average value: 86.2 MPa Grade Count:13
Cushion 0.635 cm
0.250 in
Average value: 0.635 cm Grade Count:3