Plastcom SLOVAMID 66 T 30 Polyamide 66, 30% Mineral Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Mineral Filled
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVAMID
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVAMID 66 T 30 Polyamide 66, 30% Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesPA 66 with the content of 30% chemically modified mineral filler. Used for holders of electric hand tools, hobby tools, gears, covers of electric tools, flat products, automobile wheel covers. High tensile strength and modulus. Excellent dimensional stability. Delivered in natural and in the full RAL color scale.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
STN 64 0111
Linear Mold Shrinkage 0.0134 cm/cm
0.0134 in/in
STN 64 0808
Linear Mold Shrinkage, Transverse 0.0137 cm/cm
0.0137 in/in
STN 64 0808
Melt Flow 3.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
3.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa
10200 psi
STN EN ISO 527-2
Elongation at Break 3.0 %
3.0 %
STN EN ISO 527-2
Tensile Modulus 5.30 GPa
769 ksi
STN EN ISO 527-2
Flexural Strength 115 MPa
16700 psi
STN EN ISO 178
Flexural Modulus 5.30 GPa
769 ksi
STN EN ISO 178
Charpy Impact Unnotched 3.70 J/cm²

@Temperature 23.0 °C
17.6 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
4.10 J/cm²

@Temperature -20.0 °C
19.5 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
Charpy Impact, Notched 0.200 J/cm²

@Temperature -20.0 °C
0.952 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
0.300 J/cm²

@Temperature 23.0 °C
1.43 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
DSC; STN EN ISO 3146
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
STN EN ISO 75/A
Vicat Softening Point 240 °C
464 °F
B; STN EN ISO 306
Flammability, UL94 HB
HB
Glow Wire Test 650 °C
1200 °F
STN IEC 60695-2-10
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
STN IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
STN IEC 60093
Dielectric Strength 40.0 kV/mm
1020 kV/in
STN IEC 60243
Comparative Tracking Index 500 V
500 V
STN 34 6468
Processing Properties Metric English Comments
Melt Temperature 280 - 310 °C
536 - 590 °F
Mold Temperature 80.0 - 120 °C
176 - 248 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.15 %
0.15 %
STN EN ISO 960
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi