Polymer Resources PEI-GP1 Polyetherimide, General Purpose, Unreinforced  (Unverified Data**)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PEI-GP1 Polyetherimide, General Purpose, Unreinforced  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 5.0 - 30 g/10 min
5.0 - 30 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 103 MPa
15000 psi
ASTM D638
Tensile Strength, Yield 103 MPa
15000 psi
ASTM D638
Flexural Strength 145 MPa
21000 psi
ASTM D790
Flexural Modulus 3.24 GPa
470 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm
1.00 ft-lb/in
ASTM D256
Gardner Impact >= 36.2 J
>= 26.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 204 °C
400 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 196 °C
385 °F
ASTM D648
Flammability, UL94 V-0
V-0
1/16 in
V-0
V-0
1/8 in
Processing Properties Metric English Comments
Rear Barrel Temperature 332 - 399 °C
630 - 750 °F
Middle Barrel Temperature 338 - 399 °C
640 - 750 °F
Front Barrel Temperature 343 - 399 °C
650 - 750 °F
Melt Temperature 338 - 399 °C
640 - 750 °F
Mold Temperature 107 - 177 °C
225 - 350 °F
Drying Temperature 143 - 149 °C
290 - 300 °F
Dry Time 4 - 6 hour
4 - 6 hour