Premix Premi-Glas® 1100V-15 Fiberglass Reinforced Thermoset BMC

Category Polymer , Thermoset , Filled/Reinforced Thermoset
Manufacturer Premix
Trade Name Premi-Glas®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Premi-Glas® 1100V-15 Fiberglass Reinforced Thermoset BMC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Premi-Glas® 1100V-15 is a fiberglass reinforced thermoset bulk molding compound for electrical and flame retardant applications.Key features and benefits are:Non-Halogen FR technology for regulatory complianceGood dimensional stability, including excellent thermal resistanceRecognized by Underwriter's Laboratories, File #E42524Pigmentable for molded-in color, best appearance with mold textureDesigned for compression or injection molding in matched metal die molds.Information provided by Premix.
Physical Properties Metric English Comments
Specific Gravity 1.70 - 1.85 g/cc
1.70 - 1.85 g/cc
Linear Mold Shrinkage 0.0015 - 0.0035 cm/cm
0.0015 - 0.0035 in/in
Polymerization Shrinkage
Mechanical Properties Metric English Comments
Tensile Strength 31.0 MPa
4500 psi
ASTM D638
Tensile Modulus 14.0 GPa
2030 ksi
ASTM D638
Flexural Strength 95.0 MPa
13800 psi
ASTM D790
Flexural Modulus 9.70 GPa
1410 ksi
ASTM D790
Poissons Ratio 0.30
0.30
Shear Modulus 5.40 GPa
783 ksi
Calculated
Izod Impact, Notched 3.70 J/cm
6.93 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.80 J/cm
8.99 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 35.0 µm/m-°C
19.4 µin/in-°F
Z Direction
CTE, linear, Transverse to Flow 25.0 µm/m-°C
13.9 µin/in-°F
XY Direction
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
UL RTI, Electrical 130 °C
266 °F
UL 746C
UL RTI, Mechanical with Impact 130 °C
266 °F
UL 746C
UL RTI, Mechanical without Impact 130 °C
266 °F
UL 746C
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Dielectric Strength 15.0 kV/mm
381 kV/in
ASTM D149
Arc Resistance 180 sec
180 sec
ASTM D495
Processing Properties Metric English Comments
Processing Temperature 150 °C
302 °F
Compression or Injection Molding
Clamp Pressure 3.45 - 6.89 MPa
500 - 1000 psi
Molding Pressure