Ravago Manufacturing Americas Hybrid S464LG Acrylonitrile Butadiene Styrene + PC Alloy

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Ravago Manufacturing Americas, LLC
Trade Name Hybrid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ravago Manufacturing Americas Hybrid S464LG Acrylonitrile Butadiene Styrene + PC Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Available in North America Good Toughness Low Gloss RoHS Compliant Form: Pellets Processing Method: Injection Molding Automotive Specifications: Chrysler MS-DB300 CPN4352 Color: Natural, Chrysler MS-DB300 CPN4352 Color: DX9 BLACK Black 056Information provided by Ravago
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
ASTM D792
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955 and ISO 294-4
Melt Flow 15 g/10 min

@Load 5.00 kg,
Temperature 260 °C
15 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 51.4 MPa
7450 psi
ISO 527-2
51.7 MPa
7500 psi
ASTM D638
Elongation at Break 55 %
55 %
ASTM D638
55 %
55 %
ISO 527-2
Flexural Yield Strength 75.8 MPa
11000 psi
ASTM D790
Flexural Modulus 2.21 GPa
320 ksi
ASTM D790
2.23 GPa
323 ksi
ISO 178
Izod Impact, Notched 5.34 J/cm
10.0 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 37.8 kJ/m²
18.0 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
Unannealed; ASTM D648
112 °C
234 °F
Unannealed; ISO 75-2/A
Processing Properties Metric English Comments
Rear Barrel Temperature 232 - 243 °C
450 - 470 °F
Middle Barrel Temperature 238 - 260 °C
460 - 500 °F
Front Barrel Temperature 243 - 271 °C
470 - 520 °F
Nozzle Temperature 243 - 271 °C
470 - 520 °F
Mold Temperature 65.6 - 82.2 °C
150 - 180 °F
Drying Temperature 104 - 110 °C

@Time 7200 - 14400 sec
220 - 230 °F

@Time 2.00 - 4.00 hour
Dry Time <= 10.0 hour
<= 10.0 hour
Moisture Content <= 0.040 %
<= 0.040 %
Suggested Maximum
Injection Pressure 5.52 - 12.4 MPa
800 - 1800 psi
Back Pressure 0.345 - 1.03 MPa
50.0 - 150 psi
Shot Size 40 - 80 %
40 - 80 %
Screw Speed 40 - 60 rpm
40 - 60 rpm
Descriptive Properties Value Comments
Injection Rate Moderate
Melt-Volume Flow Rate, 260°C/5.0 kg (in3/10 min) 0.854
ISO 1133