SABIC HP0322N Low Density Polyethylene for Blown Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer SABIC
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC HP0322N Low Density Polyethylene for Blown Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: HP0322N is a Low Density Polyethylene grade suitable for producing heavy duty films and contains no slip or antiblock additives. It yields outstanding toughness and optical properties in the film.Typical Applications: HP0322N can be used for heavy duty bags, industrial shrink films, construction and agricultural films.Information provided by SABIC.
Physical Properties Metric English Comments
Density 0.922 g/cc
0.0333 lb/in³
ASTM D1505
Thickness 50.0 microns
1.97 mil
Melt Flow 0.30 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.30 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.0 MPa
1600 psi
ASTM D882
Film Tensile Strength at Yield, TD 10.0 MPa
1450 psi
ASTM D882
Film Elongation at Break, MD 450 %
450 %
ASTM D882
Film Elongation at Break, TD 690 %
690 %
ASTM D882
Elmendorf Tear Strength MD 400 g
400 g
ASTM D1922
Elmendorf Tear Strength TD 300 g
300 g
ASTM D1922
Elmendorf Tear Strength, MD 8.00 g/micron
203 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 6.00 g/micron
152 g/mil
ASTM D1922
Dart Drop 4.00 g/micron
102 g/mil
ASTM D1709
Dart Drop Test 200 g
0.441 lb
ASTM D1709
Film Tensile Strength at Break, MD 31.0 MPa
4500 psi
ASTM D882
Film Tensile Strength at Break, TD 30.0 MPa
4350 psi
ASTM D882
1% Secant Modulus, MD 190 MPa
27600 psi
ASTM D882
1% Secant Modulus, TD 220 MPa
31900 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 95.0 °C
203 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 11 %
11 %
ASTM D1003
Gloss 50 %
50 %
at 45°; ASTM D2457
Processing Properties Metric English Comments
Melt Temperature 180 - 195 °C
356 - 383 °F
Blow-up Ratio (BUR) 2.5 - 4.0
2.5 - 4.0