SABIC Innovative Plastics Cycoloy® CX7510 PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CX7510 PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cycoloy* CX7510 resin is an injection moldable, flame retardant PC/ABS blend, with non-chlorinated & non-brominated flame retardants. Key features of Cycoloy CX7510 resin include high heat, high flow and good impact resistance.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D 792
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.050 %
0.050 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.11 %

@Temperature 23.0 °C
0.11 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0056 - 0.0063 cm/cm

@Thickness 3.20 mm
0.0056 - 0.0063 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 16 g/10 min

@Load 2.16 kg,
Temperature 260 °C
16 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D 1238
41 g/10 min

@Load 5.00 kg,
Temperature 260 °C
41 g/10 min

@Load 11.0 lb,
Temperature 500 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
45 g/10 min

@Load 5.00 kg,
Temperature 260 °C
45 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 48.0 MPa
6960 psi
50 mm/min; ISO 527
49.0 MPa
7110 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 64.0 MPa
9280 psi
50 mm/min; ISO 527
65.0 MPa
9430 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 36 %
36 %
Type I, 50 mm/min; ASTM D 638
36 %
36 %
50 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
Type I, 50 mm/min; ASTM D 638
4.5 %
4.5 %
50 mm/min; ISO 527
Tensile Modulus 2.54 GPa
368 ksi
1 mm/min; ISO 527
2.58 GPa
374 ksi
50 mm/min; ASTM D 638
Flexural Yield Strength 97.0 MPa
14100 psi
1.3 mm/min, 50 mm span; ASTM D 790
99.0 MPa
14400 psi
2 mm/min; ISO 178
Flexural Modulus 2.33 GPa
338 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.62 GPa
380 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.37 J/cm

@Temperature -30.0 °C
2.57 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
6.40 J/cm

@Temperature 23.0 °C
12.0 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Charpy Impact, Notched 3.60 J/cm²

@Temperature 23.0 °C
17.1 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 65.0 J

@Temperature 23.0 °C
47.9 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 69.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
106 °C

@Thickness 6.40 mm
223 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Vicat Softening Point 113 °C
235 °F
Rate B/50; ASTM D 1525
115 °C
239 °F
Rate B/50; ISO 306
118 °C
244 °F
Rate B/120; ISO 306
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94
5VB

@Thickness 1.50 mm
5VB

@Thickness 0.0591 in
UL 94