SABIC Innovative Plastics LNP LUBRICOMP DP003 PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DP003 PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* DP003 is a compound based on Polycarbonate resin containing Silicone, PTFE. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.26 g/cc
0.0455 lb/in³
ASTM D792
1.26 g/cc
0.0455 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
0.190 %
0.190 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0080 - 0.010 cm/cm

@Time 86400 sec
0.0080 - 0.010 in/in

@Time 24.0 hour
ISO 294
0.0090 - 0.010 cm/cm

@Time 86400 sec
0.0090 - 0.010 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.010 - 0.012 cm/cm

@Time 86400 sec
0.010 - 0.012 in/in

@Time 24.0 hour
ASTM D955
0.010 - 0.012 cm/cm

@Time 86400 sec
0.010 - 0.012 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 41.0 MPa
5950 psi
ISO 527
42.0 MPa
6090 psi
ASTM D638
Tensile Strength, Yield 48.0 MPa
6960 psi
ASTM D638
49.0 MPa
7110 psi
ISO 527
Elongation at Break 35.1 %
35.1 %
ASTM D638
41.2 %
41.2 %
ISO 527
Elongation at Yield 5.6 %
5.6 %
ASTM D638
5.8 %
5.8 %
ISO 527
Tensile Modulus 2.16 GPa
313 ksi
1 mm/min; ISO 527
2.23 GPa
323 ksi
50 mm/min; ASTM D638
Flexural Strength 75.0 MPa
10900 psi
ASTM D790
75.0 MPa
10900 psi
ISO 178
Flexural Modulus 1.84 GPa
267 ksi
ISO 178
1.89 GPa
274 ksi
ASTM D790
Izod Impact, Notched 2.83 J/cm
5.30 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 31.0 kJ/m²
14.8 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*4; ISO 180/1U
Dart Drop, Total Energy 28.0 J
20.7 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 61.0 J
45.0 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.10
0.10
ASTM D3702 Modified
Coefficient of Friction, Static 0.26
0.26
ASTM D3702 Modified
K (wear) Factor 84.6 x 10-8 mm³/N-M
42.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
264 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
127 °C

@Thickness 3.20 mm
261 °F

@Thickness 0.126 in
unannealed; ASTM D648