SABIC Innovative Plastics LNP LUBRICOMP WL004 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP WL004 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* WL004 is a compound based on PBT resin containing 20% PTFE. Added features of this material include: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0500 % | 0.0500 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0800 % | 0.0800 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.021 - 0.024 cm/cm @Time 86400 sec |
0.021 - 0.024 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0244 - 0.0254 cm/cm @Time 86400 sec |
0.0244 - 0.0254 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0214 - 0.023 cm/cm @Time 86400 sec |
0.0214 - 0.023 in/in @Time 24.0 hour |
ISO 294 |
| 0.021 - 0.024 cm/cm @Time 86400 sec |
0.021 - 0.024 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ISO 527 |
| 48.0 MPa | 6960 psi | ASTM D638 | |
| Elongation at Break | 8.4 % | 8.4 % | ISO 527 |
| 9.8 % | 9.8 % | ASTM D638 | |
| Tensile Modulus | 2.41 GPa | 350 ksi | 50 mm/min; ASTM D638 |
| 2.44 GPa | 354 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 77.0 MPa | 11200 psi | ISO 178 |
| 78.0 MPa | 11300 psi | ASTM D790 | |
| Flexural Modulus | 2.39 GPa | 347 ksi | ISO 178 |
| 2.41 GPa | 350 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.37 J/cm | 8.19 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.33 | 0.33 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.24 | 0.24 | ASTM D3702 Modified |
| K (wear) Factor | 117 x 10-8 mm³/N-M | 58.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 89.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 89.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 95.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
53.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 95.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
53.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 55.0 °C @Thickness 3.20 mm |
131 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN EH 96 FRD 2 PP, flame retardant
- Plastcom SLOVAMID 6 NG1 GF 20 HLS PA6, 20% glass fibre, combined stability
- NOVA Chemicals Sclair® 10B Octene VLDPE Film Resin (discontinued **)
- Gouda Vuurvast A 1 S Dense Refractory Brick
- Techmer ES HiFill® PA6 GF HS UV 33% Glass Filled
- Stellarchem DIOSHY® GP-935-UB2 TPE Compound
- Toyobo PELPRENE™ P55B Polyester TPE
- E-Polymers TEKAMID® TA210F Fast Crystallinity PA66, DAM
- Akzo Nobel Trigonox® ADC-NS60 Polymerization Initiator
- 3A Composites Core Materials AIREX® C70.250 Universal Structural Foam
Copyright © lookpolymers.com All Rights Reserved