Solvay Specialty Polymers Ryton® R-4-240NA Polyphenylene Sulfide (PPS), 40% Glass Fiber

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Manufacturer Solvay Specialty Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ryton® R-4-240NA Polyphenylene Sulfide (PPS), 40% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ryton® R-4-240NA and R-4-240BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength and toughness compared to other polyphenylene sulfide compounds.Features: Good Strength; Good ToughnessInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.66 g/cc
0.0600 lb/in³
ASTM D792
Filler Content 40 %
40 %
Glass Fiber
Water Absorption 0.020 %

@Time 86400 sec
0.020 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0020 cm/cm

@Thickness 3.18 mm
0.0020 in/in

@Thickness 0.125 in
Linear Mold Shrinkage, Transverse 0.0050 cm/cm

@Thickness 3.20 mm
0.0050 in/in

@Thickness 0.126 in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 99
99
ASTM D785
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength 172 MPa
24900 psi
ASTM D638
Tensile Stress 185 MPa
26800 psi
ISO 527-2
Elongation at Break 1.9 %
1.9 %
ASTM D638
2.0 %
2.0 %
ISO 527-2
Flexural Strength 262 MPa
38000 psi
ASTM D790
275 MPa
39900 psi
ISO 178
Flexural Modulus 13.8 GPa
2000 ksi
ASTM D790
14.0 GPa
2030 ksi
ISO 178
Compressive Strength 265 MPa
38400 psi
ASTM D695
Poissons Ratio 0.39
0.39
ASTM E132
Izod Impact, Notched 0.910 J/cm

@Thickness 3.18 mm
1.70 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 8.00 J/cm

@Thickness 3.18 mm
15.0 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
Notch A; ISO 180
Izod Impact, Unnotched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 µm/m-°C

@Temperature 100 - 200 °C
8.33 µin/in-°F

@Temperature 212 - 392 °F
2
20.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
11.1 µin/in-°F

@Temperature -58.0 - 122 °F
2
CTE, linear, Transverse to Flow 40.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
22.2 µin/in-°F

@Temperature -58.0 - 122 °F
TMA; ASTM E831
90.0 µm/m-°C

@Temperature 100 - 200 °C
50.0 µin/in-°F

@Temperature 212 - 392 °F
TMA; ASTM E831
Thermal Conductivity 0.310 W/m-K
2.15 BTU-in/hr-ft²-°F
ASTM C177
Maximum Service Temperature, Air 200 - 220 °C
392 - 428 °F
UL Temperature Rating
Deflection Temperature at 1.8 MPa (264 psi) 265 °C
509 °F
Unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
5VA

@Thickness 1.60 mm
5VA

@Thickness 0.0630 in
Oxygen Index 54 %
54 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
ASTM D257
Insulation Resistance 1.00e+12 ohm

@Temperature 90.0 °C
1.00e+12 ohm

@Temperature 194 °F
IEC 60167
Dielectric Constant 3.9

@Frequency 1000 Hz
3.9

@Frequency 1000 Hz
ASTM D150
4.0

@Frequency 1.00e+6 Hz
4.0

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 22.0 kV/mm
559 kV/in
ASTM D149
Dissipation Factor 0.0020

@Frequency 1000 Hz
0.0020

@Frequency 1000 Hz
ASTM D150
0.0020

@Frequency 1.00e+6 Hz
0.0020

@Frequency 1.00e+6 Hz
ASTM D150
Arc Resistance 130 sec
130 sec
ASTM D495
Comparative Tracking Index 150 V
150 V
UL 746
Descriptive Properties Value Comments
Availability Asia Pacific
Europe
Latin America
North America
Color Natural
Form Pellets
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant