Solvay TECHNYL® A 20 V25 PA66, 25% glass fiber, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Solvay
Trade Name Technyl®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® A 20 V25 PA66, 25% glass fiber, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: TECHNYL® A 20 V25 is a 25% glass fiber reinforced Red Phosphorous flame retarded grade based on a polyamide 66 resin. This product is heat stabiised for optimised injection moulding. This product is available in Natural & Black. Key Properties: UL94 V0 at 0.8mm and Excellent filling qualitiesBenefits: This Red Phosphorous flame retardent grade provides robust UL 94 V-0 and a full UL yellow card while offering good mechanical properties. This grade is suitable for moulding insulating parts for electrical devices, and more generally for thin parts under stress. Available in: Asia Pacific, Europe, Latin America and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/E.C.This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applicationsApplications: Industrial controls and electrical insulation systemInformation provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
ISO 1183/A
Water Absorption 0.75 %

@Temperature 23.0 °C,
Time 86400 sec
0.75 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Viscosity 110 cP

@Shear Rate 1000 1/s,
Temperature 300 °C
110 cP

@Shear Rate 1000 1/s,
Temperature 572 °F
200 cP

@Shear Rate 1000 1/s,
Temperature 280 °C
200 cP

@Shear Rate 1000 1/s,
Temperature 536 °F
200 cP

@Shear Rate 100 1/s,
Temperature 300 °C
200 cP

@Shear Rate 100 1/s,
Temperature 572 °F
300 cP

@Shear Rate 100 1/s,
Temperature 280 °C
300 cP

@Shear Rate 100 1/s,
Temperature 536 °F
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
Isotropy
Linear Mold Shrinkage, Flow 0.0050 cm/cm
0.0050 in/in
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
ISO 527 Type 1A
Tensile Stress 30.0 MPa

@Strain 0.500 %
4350 psi

@Strain 0.500 %
95.0 MPa

@Strain 1.00 %
13800 psi

@Strain 1.00 %
130 MPa

@Strain 1.50 %
18900 psi

@Strain 1.50 %
150 MPa

@Strain 2.00 %
21800 psi

@Strain 2.00 %
170 MPa

@Strain 2.50 %
24700 psi

@Strain 2.50 %
Elongation at Break 2.0 %
2.0 %
ISO 527 Type 1A
Tensile Modulus 9.00 GPa
1310 ksi
ISO 527 Type 1A
Flexural Strength 250 MPa
36300 psi
ISO 178
Flexural Modulus 7.50 GPa
1090 ksi
ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 5.00 J/cm²
23.8 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 5.40 µm/m-°C

@Temperature 23.0 - 85.0 °C
3.00 µin/in-°F

@Temperature 73.4 - 185 °F
ISO 11359
Melting Point 263 °C
505 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
ISO 75/Af
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
ISO 1210
V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
ISO 1210
V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
ISO 1210
Oxygen Index 30.5 %
30.5 %
ISO 4589
Glow Wire Test 725 °C
1340 °F
Ignition Temperature; ISO 60695-2-13
960 °C
1760 °F
ISO 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Strength 25.0 kV/mm
635 kV/in
IEC 60243
Dissipation Factor 0.020
0.020
IEC 60250
Comparative Tracking Index 250 V
250 V
Solution B; IEC 60112
300 V
300 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 270 - 275 °C
518 - 527 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 275-280°C
Fire and smoke F index I3/F3
NF F 16 101
Mixing Zone 280-285°C