Styrolution Luran® 378 P G7 35% Glass Filled SAN

Category Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded, Glass Reinforced
Manufacturer Styrolution
Trade Name Luran®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styrolution Luran® 378 P G7 35% Glass Filled SAN.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Glass-reinforced grade with very high stiffness and low thermal coefficient of liner expansion.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.25 %
0.25 %
23°C/50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
Melt Flow 5.44 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 5.44 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ISO 1133
5.44 g/10 min

@Load 21.6 kg,
Temperature 200 °C
 5.44 g/10 min

@Load 47.6 lb,
Temperature 392 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 93
93
ISO 2039-2
Ball Indentation Hardness 240 MPa

@Load 36.5 kg,
Time 30.0 sec
 34800 psi

@Load 80.5 lb,
Time 0.00833 hour
 ISO 2039-1
Tensile Strength at Break 110 MPa
16000 psi
ISO 527-1/-2
Elongation at Break 2.0 %
2.0 %
ISO 527-1/-2
Tensile Modulus 12.0 GPa
1740 ksi
ISO 527-1/-2
Flexural Strength 150 MPa
21800 psi
ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
ISO 180/A
Charpy Impact Unnotched 1.70 J/cm²

@Temperature 23.0 °C
 8.09 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.400 J/cm²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Tensile Creep Modulus, 1000 hours 7500 MPa

@Strain <=0.500 %
 1.09e+6 psi

@Strain <=0.500 %
 ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 13.9 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-1/-2
Thermal Conductivity 0.190 W/m-K
1.32 BTU-in/hr-ft²-°F
DIN 52612-1
Maximum Service Temperature, Air 90.0 °C
194 °F
Deflection Temperature at 0.46 MPa (66 psi) 108 °C
226 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 104 °C
219 °F
ISO 75-1/-2
Vicat Softening Point 109 °C
228 °F
VST B50; ISO 306
Flammability, UL94 HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 IEC 60695-11-10
HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
 3.2

@Frequency 1.00e+6 Hz
 IEC 60250
3.5

@Frequency 100 Hz
 3.5

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 39.0 kV/mm
991 kV/in
K20/P50; IEC 60243-1
Dissipation Factor 0.0070

@Frequency 100 Hz
 0.0070

@Frequency 100 Hz
 IEC 60250
0.010

@Frequency 1.00e+6 Hz
 0.010

@Frequency 1.00e+6 Hz
 IEC 60250
Processing Properties Metric English Comments
Melt Temperature 220 - 260 °C
428 - 500 °F
Injection Molding
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Pre-drying
Dry Time 2 - 4 hour
2 - 4 hour
Pre-drying
Descriptive Properties Value Comments
Color Natural
Commercial Status Europe
Primary Processing Technique Injection Molding and Extrusion