Sumitomo Bakelite North America FS-10-VO-P Short-Glass Reinforced Diallyl Phthalate

Category Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled , Filled/Reinforced Thermoset
Manufacturer Sumitomo Bakelite North America
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Sumitomo Bakelite North America FS-10-VO-P Short-Glass Reinforced Diallyl Phthalate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Isophthalate DAP Resin Isomer. Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type SIG-F.Information provided by Sumitomo Bak North America, Inc.
Physical Properties Metric English Comments
Density 1.95 g/cc
0.0704 lb/in³
ASTM D792
Apparent Bulk Density 0.800 g/cc
0.0289 lb/in³
Water Absorption 0.25 %
0.25 %
48 hours, 50°C. ASTM D570
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Compression Molding. ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 83.0 MPa
12000 psi
ASTM D638
Flexural Yield Strength 115 MPa
16700 psi
ASTM D790
Flexural Modulus 18.0 GPa
2610 ksi
ASTM D790
Compressive Yield Strength 180 MPa
26100 psi
ASTM D695
Izod Impact, Notched 0.330 J/cm
0.618 ft-lb/in
ASTM D256A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 18.0 µm/m-°C

@Temperature 20.0 °C
10.0 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Maximum Service Temperature, Air 130 °C
266 °F
UL temperature Index, UL 746B
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
as molded; ASTM D648
UL RTI, Electrical 130 °C
266 °F
UL temperature Index, UL 746B
UL RTI, Mechanical with Impact 130 °C
266 °F
UL temperature Index, UL 746B
UL RTI, Mechanical without Impact 130 °C
266 °F
UL temperature Index, UL 746B
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
Oxygen Index 50 %
50 %
ASTM D2863
Electrical Properties Metric English Comments
Dielectric Constant 3.9

@Frequency 1e+6 Hz
3.9

@Frequency 1e+6 Hz
Wet
Dielectric Strength 13.5 kV/mm

@Frequency 60.0 Hz
343 kV/in

@Frequency 60.0 Hz
Wet, step by step; ASTM D149
Dissipation Factor 0.020

@Frequency 1e+6 Hz
0.020

@Frequency 1e+6 Hz
Wet; ASTM D150
Arc Resistance 130 sec
130 sec
ASTM D495
Comparative Tracking Index >= 600 V
>= 600 V
ASTM D3638 (IEC 112)
Processing Properties Metric English Comments
Processing Temperature 160 - 180 °C
320 - 356 °F
Mold temperature
Descriptive Properties Value Comments
Flammability, Burning, sec 50
ASTM D229
Flammability, Ignition, sec 130
ASTM D229