- Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled
- Sumitomo Bakelite North America RX® 2-520 Short-Glass Reinforced Diallyl Phthalate
Sumitomo Bakelite North America RX® 2-520 Short-Glass Reinforced Diallyl Phthalate
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled , Filled/Reinforced Thermoset |
| Manufacturer | Sumitomo Bakelite North America |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite North America RX® 2-520 Short-Glass Reinforced Diallyl Phthalate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Isophthalate DAP Resin Isomer. Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type SIGInformation provided by Sumitomo Bak North America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.91 g/cc | 0.0690 lb/in³ | ASTM D792 |
| Water Absorption | 0.35 % | 0.35 % | 48 hours, 50°C. ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | Compression Molding. ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638 |
| Flexural Yield Strength | 120 MPa | 17400 psi | ASTM D790 |
| Flexural Modulus | 17.8 GPa | 2580 ksi | ASTM D790 |
| Compressive Yield Strength | 165 MPa | 23900 psi | ASTM D695 |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.0 µm/m-°C @Temperature 20.0 °C |
10.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | UL temperature Index, UL 746B |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 260 °C | >= 500 °F | as molded; ASTM D648A |
| UL RTI, Electrical | 130 °C | 266 °F | UL temperature Index, UL 746B |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | UL temperature Index, UL 746B |
| UL RTI, Mechanical without Impact | 130 °C | 266 °F | UL temperature Index, UL 746B |
| Oxygen Index | 25 % | 25 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
Wet |
| Dielectric Strength | 13.5 kV/mm @Frequency 60.0 Hz |
343 kV/in @Frequency 60.0 Hz |
Wet, step by step; ASTM D149 |
| Dissipation Factor | 0.017 @Frequency 1e+6 Hz |
0.017 @Frequency 1e+6 Hz |
Wet; ASTM D150 |
| Arc Resistance | 150 sec | 150 sec | ASTM D495 |
| Hot Wire Ignition, HWI | 7.0 - 14 sec @Thickness 1.47 mm |
7.0 - 14 sec @Thickness 0.0579 in |
UL PLC 4 (7-14 sec) |
| High Amp Arc Ignition, HAI | 15 - 29 arcs @Thickness 1.47 mm |
15 - 29 arcs @Thickness 0.0579 in |
UL PLC 3 (15-29 arcs) |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 10.0 mm/min @Thickness 1.47 mm |
0.000 - 0.394 in/min @Thickness 0.0579 in |
UL PLC 0 (0-10 mm/min) |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 160 - 180 °C | 320 - 356 °F | Mold temperature |