Toyobo Pelprene™ S-1001 Polyester TPE

Category Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer Toyobo
Trade Name Pelprene™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Toyobo Pelprene™ S-1001 Polyester TPE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Key Feature: Pelprene S typePelprene™ can be processed into a wide variety of articles from ultra-small precision parts to sheets by injection, extrusion, and blow molding. The 'S' type is a block copolymer consisting of an aromatic polyester as the hard segment and an aliphatic polyester as the soft one. It has physical properties similar to the 'P' type and excellent heat aging and weather resistance.Information provided by Toyobo Co., Ltd
Physical Properties Metric English Comments
Density 1.21 g/cc
0.0437 lb/in³
ASTM D792
Moisture Absorption at Equilibrium 0.40 %
0.40 %
25°C; 65%RH
Linear Mold Shrinkage 0.012 cm/cm

@Thickness 2.00 mm
0.012 in/in

@Thickness 0.0787 in
Melt Flow 18 g/10 min

@Temperature 190 °C
18 g/10 min

@Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 96
96
ASTM D2240
Hardness, Shore D 48
48
ASTM D2240
Tensile Strength, Ultimate 30.0 MPa
4350 psi
ASTM D638
Elongation at Break 730 %
730 %
ASTM D638
50% Modulus 0.0108 GPa
1.57 ksi
ASMT D638
Flexural Modulus 0.125 GPa
18.1 ksi
ASTM D790
Compressive Modulus 0.0100 GPa
1.45 ksi
10% Compression Modulus; ASTM D695
Resilience 63
63
JIS K6301
Izod Impact, Notched NB
NB
ASTM D256
Tear Strength 118 kN/m
673 pli
ASTM D624
Taber Abrasion, mg/1000 Cycles 15
15
CS-17 wheel; ASTM D1044
Compression Set 60 %

@Temperature 70.0 °C
60 %

@Temperature 158 °F
70°C; 22 hrs; JIS K6301
Thermal Properties Metric English Comments
CTE, linear 190 µm/m-°C

@Temperature 20.0 °C
106 µin/in-°F

@Temperature 68.0 °F
TMA
Melting Point 200 °C
392 °F
DSC
Deflection Temperature at 1.8 MPa (264 psi) 68.0 °C
154 °F
ASTM D648
Vicat Softening Point 172 °C
342 °F
ASTM D1525
Brittleness Temperature -65.0 °C
-85.0 °F
JIS K6301
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Electrical Resistivity 2.00e+12 ohm-cm
2.00e+12 ohm-cm
ASTM D257
Dielectric Strength 25.0 kV/mm
635 kV/in
JIS K2111