Tra-Con Tra-Bond 2119 Low Viscosity Glass Laminating Adhesive

Category	Polymer , Adhesive , Thermoset
Manufacturer	Tra-Con, Inc.
Trade Name	Tra-Bond
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Tra-Con Tra-Bond 2119 Low Viscosity Glass Laminating Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

TRA-BOND 2119 is a crystal clear adhesive specifically designed for bonding glass to glass and glass to plastics. It also yields a high lap shear strength to metals and ceramics. This system cures to a semi-rigid hardness making it ideal for bonding dissimilar substrates especially when thermal cycling is required. This two part adhesive also has a low exotherm and therefore can be used for small pottings and filling bond gaps up to 1/8 inch. Information provided by Tra-Con Inc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.06 g/cc	1.06 g/cc	Mixed
Volatile Organic Compounds (VOC) Content	87.7 g/l	87.7 g/l
Water Absorption	0.49 %	0.49 %	After 24 hours
Viscosity	500 cP @Temperature 25.0 °C	500 cP @Temperature 77.0 °F	Mixed (sp #4, 12 rpm)

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	76	76	24 hrs @ 25°C
	79	79	1 hr @ 65°C
	80	80	2 hrs @ 65°C
Adhesive Bond Strength	12.1 MPa	1750 psi	Lap shear, alum to alum, 24 hrs @ 25°C
	15.9 MPa	2300 psi	Lap shear, alum to alum, 1 hr @ 65°C
	18.3 MPa	2650 psi	Lap shear, alum to alum, 2 hrs @ 65°C

Thermal Properties	Metric	English	Comments
CTE, linear	88.8 µm/m-°C	49.3 µin/in-°F	Below Tg
	241 µm/m-°C	134 µin/in-°F	Above Tg
Glass Transition Temp, Tg	95.0 °C	203 °F	Ultimate Tg

Optical Properties	Metric	English	Comments
Refractive Index	1.53	1.53

Processing Properties	Metric	English	Comments
Cure Time	60.0 - 120 min @Temperature 65.0 °C	1.00 - 2.00 hour @Temperature 149 °F
	1440 min @Temperature 25.0 °C	24.0 hour @Temperature 77.0 °F
Pot Life	45 min	45 min	25 grams

Descriptive Properties	Value	Comments
Color	Clear
Thixotropic Index	1	6 rpm/60 rpm
Working Life hours	2	25 grams