Tra-Con Tra-Bond 516H01 Low Viscosity Room Temperature Cure Adhesive

Category Polymer , Adhesive , Thermoset
Manufacturer Tra-Con, Inc.
Trade Name Tra-Bond
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Tra-Con Tra-Bond 516H01 Low Viscosity Room Temperature Cure Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TRA-BOND 516H01 is a room temperature curing, low viscosity adhesive formulated for terminating ALL TYPES of fiber optic connectors, including Pre-Mixed and Frozen applications. It has also been used for bonding LED displays, lenses and other optical components. TRA-BOND 516H01 provides both high bond strength as well as low stress connections with no pistoning. TRA-BOND 516H01 is provided in a dark blue color to allow easy polishing. Information provided by Tra-Con Inc.
Physical Properties Metric English Comments
Viscosity 450 cP
450 cP
Mixed (cp #40, 10 rpm)
Mechanical Properties Metric English Comments
Hardness, Shore D 70
70
1 hr @ 65°C
71
71
24 hrs @ 25°C
75
75
4 hrs @ 65°C
75
75
72 hrs @ 25°C
Adhesive Bond Strength 5.03 MPa
730 psi
Lap shear, alum to alum, 24 hrs @ 25°C
8.76 MPa
1270 psi
Lap shear, alum to alum, 72 hrs @ 25°C
9.51 MPa
1380 psi
Lap shear, alum to alum, 1 hr @ 65°C
20.3 MPa
2950 psi
Lap shear, alum to alum, 4 hrs @ 65°C
Thermal Properties Metric English Comments
CTE, linear 67.0 µm/m-°C
37.2 µin/in-°F
Below Tg
212 µm/m-°C
118 µin/in-°F
Above Tg
Glass Transition Temp, Tg 49.0 °C
120 °F
Ultimate Tg; TMA
Processing Properties Metric English Comments
Cure Time 60.0 - 240 min

@Temperature 65.0 °C
1.00 - 4.00 hour

@Temperature 149 °F
1440 - 4320 min

@Temperature 25.0 °C
24.0 - 72.0 hour

@Temperature 77.0 °F
Descriptive Properties Value Comments
Color Clear
Resin
Dark Blue
Hardener/Mixed/Cured