Zyvex Performance Materials Aroply™ 350 Nano-Engineered Composite Film Adhesive

Category Polymer , Thermoset , Carbon Fiber/Thermoset Composite
Manufacturer Zyvex Performance Materials (ZPM)
Trade Name Aroply™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zyvex Performance Materials Aroply™ 350 Nano-Engineered Composite Film Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Aroply™ 350 Film Adhesive is a versatile, heat curing carbon-nanotube modified epoxy structural film adhesive available in a variety of film weights on a supported carrier. Cured adhesive characteristics are designated by exceptionally high shear and peel strengths on a variety of substrates at temperatures up to 350F. This film adhesive is designed for both solid panel and honeycomb constructions. Aroply™ 350 contains an optimum level of carbon nanotubes for additional toughness and enhanced mechanical properties. The carbon nanotubes use molecular dispersion technology to ensure enhancements are evenly distributed throughout the adhesive. Features: Semi-tacky for adherence to desired location Long Open Time: 30 days in standard shop conditions Adaptable to many processes
Physical Properties Metric English Comments
Viscosity 1000 cP

@Temperature 120 °C
1000 cP

@Temperature 248 °F
Rheology, 2°C/min
1100 cP

@Temperature 160 °C
1100 cP

@Temperature 320 °F
Rheology, 2°C/min
8000 cP

@Temperature 80.0 °C
8000 cP

@Temperature 176 °F
Rheology, 2°C/min
800000 cP

@Temperature 40.0 °C
800000 cP

@Temperature 104 °F
Rheology, 2°C/min
1.10e+7 cP

@Temperature 175 °C
1.10e+7 cP

@Temperature 347 °F
Rheology, 2°C/min
Mechanical Properties Metric English Comments
Tensile Strength 6.89 MPa
1000 psi
Flatwise, 90 min @ 350°F, Spring Clamp Pressure, Abraded 6061-T6 Untreated; ASTM C297M
Shear Strength 10.34 MPa

@Temperature 177 °C
1500 psi

@Temperature 350 °F
2 hr soak, 90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D1002
20.68 MPa

@Temperature 177 °C
3000 psi

@Temperature 350 °F
90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D1002
26.20 MPa

@Temperature 121 °C
3800 psi

@Temperature 250 °F
90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D1002
28.96 MPa

@Temperature 21.1 °C
4200 psi

@Temperature 70.0 °F
90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D1002
Peel Strength 2.98 kN/m

@Temperature 21.1 °C
17.0 pli

@Temperature 70.0 °F
T-Peel, 90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D1876
4.56 kN/m

@Temperature 121 °C
26.0 pli

@Temperature 250 °F
T-Peel, 90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D1876
5.61 kN/m

@Temperature 177 °C
32.0 pli

@Temperature 350 °F
Roller Peel, 90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D3167
6.49 kN/m

@Temperature 21.1 °C
37.0 pli

@Temperature 70.0 °F
Roller Peel, 90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D3167
7.54 kN/m

@Temperature 121 °C
43.0 pli

@Temperature 250 °F
Roller Peel, 90 min @ 350°F, Spring Clamp Pressure, FPL Acid Etched 6061-T6; ASTM D3167
Descriptive Properties Value Comments
Drum Peel 19.8 in-lb/in
Tool Side Up, 2 hrs @ 250°F, 30 psi, 6061 T6 Abraded, 1” Nomex 3 lb core 1/8” cell
20.5 in-lb/in
Tool Side Down, 2 hrs @ 250°F, 30 psi, 6061 T6 Abraded, 1” Nomex 3 lb core 1/8” cell
Load to Failure 606 lbf
5 lb Core, 6 hrs @ 220°F, Vacuum Bag
669 lbf
8 lb Core, 6 hrs @ 220°F, Vacuum Bag