- Zyvex Performance Materials Epovex™ Nano-Engineered Composite Epoxy Adhesive Paste
Zyvex Performance Materials Epovex™ Nano-Engineered Composite Epoxy Adhesive Paste
| Category | Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive, Flexible |
| Manufacturer | Zyvex Performance Materials (ZPM) |
| Trade Name | Epovex™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Zyvex Performance Materials Epovex™ Nano-Engineered Composite Epoxy Adhesive Paste.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Epovex® Adhesive Paste is a carbon nanotube enhanced two part epoxy adhesive thixotropic paste. Used for bonding or filling, Epovex Paste is ideal for many metals, woods, masonry products, and some plastics and rubbers. Epovex Paste was also designed to bond Zyvex Technologies’ Arovex® composites.Features: Excellent flexibilityVery high T-peel strengthsVery high tensile shear strengths Non-drop, non-sag on vertical surfaces
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.980 g/cc | 0.980 g/cc | Part B |
| 1.28 g/cc | 1.28 g/cc | Part A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Shear Strength | 8.96 MPa @Temperature 82.2 °C |
1300 psi @Temperature 180 °F |
Cure cycle: 7 days @ RT , with Aced Etched 6061-T6 Aluminum |
| 12.1 MPa @Temperature 60.0 °C |
1750 psi @Temperature 140 °F |
Arovex (abraded), with Arovex Carbon Fiber Epoxy Laminate | |
| 15.2 MPa @Temperature 60.0 °C |
2210 psi @Temperature 140 °F |
Aluminum (abraded), with Arovex Carbon Fiber Epoxy Laminate | |
| 17.9 MPa @Temperature 60.0 °C |
2600 psi @Temperature 140 °F |
Cure cycle: 7 days @ RT , with Aced Etched 6061-T6 Aluminum | |
| 21.4 MPa @Temperature 23.9 °C |
3100 psi @Temperature 75.0 °F |
Cure cycle: 7 days @ RT (+7 days ethyl alcohol soak), with Aced Etched 6061-T6 Aluminum | |
| 21.4 MPa @Temperature 23.9 °C |
3100 psi @Temperature 75.0 °F |
Cure cycle: 7 days @ RT (+7 days gasoline soak) , with Aced Etched 6061-T6 Aluminum | |
| 23.7 MPa @Temperature 23.9 °C |
3440 psi @Temperature 75.0 °F |
Arovex (abraded), with Arovex Carbon Fiber Epoxy Laminate | |
| 24.1 MPa @Temperature 23.9 °C |
3500 psi @Temperature 75.0 °F |
Aluminum (abraded), with Arovex Carbon Fiber Epoxy Laminate | |
| 24.8 MPa @Temperature 23.9 °C |
3600 psi @Temperature 75.0 °F |
Cure cycle: 7 days @ RT (+7 days water soak) , with Aced Etched 6061-T6 Aluminum | |
| 25.5 MPa @Temperature 23.9 °C |
3700 psi @Temperature 75.0 °F |
Arovex (abraded) (+7 days water soak), with Arovex Carbon Fiber Epoxy Laminate | |
| 25.5 MPa @Temperature 23.9 °C |
3700 psi @Temperature 75.0 °F |
Cure cycle: 3 days @ RT, with Aced Etched 6061-T6 Aluminum | |
| 27.6 MPa @Temperature 23.9 °C |
4000 psi @Temperature 75.0 °F |
Cure cycle: 7 days @ RT, with Aced Etched 6061-T6 Aluminum | |
| 27.6 MPa @Temperature 23.9 °C |
4000 psi @Temperature 75.0 °F |
Cure cycle: 12 hrs @ RT + 1 hr @ 176°F, with Aced Etched 6061-T6 Aluminum | |
| 30.3 MPa @Temperature 23.9 °C |
4400 psi @Temperature 75.0 °F |
Cure cycle: 2 hrs @ 176°F, with Aced Etched 6061-T6 Aluminum | |
| 30.3 MPa @Temperature -40.0 °C |
4400 psi @Temperature -40.0 °F |
Cure cycle: 7 days @ RT , with Aced Etched 6061-T6 Aluminum | |
| Peel Strength | 5.26 kN/m | 30.0 pli | Cure cycle: 1 day @ RT, with Acid Etched 6061-T6 Aluminum |
| 6.14 kN/m | 35.0 pli | Cure cycle: 3 days @ RT, with Acid Etched 6061-T6 Aluminum | |
| 7.01 kN/m | 40.0 pli | Cure cycle: 12 hrs @ RT + 1 hr @ 176°F, with Acid Etched 6061-T6 Aluminum |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Amber | Part B, uncured |
| Black | Blend, uncured | |
| Black | Part A, uncured |