- LATI Latilon 28D K/40 PC, 40% Carbon Fiber Reinforced
LATI Latilon 28D K/40 PC, 40% Carbon Fiber Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Carbon Fiber Reinforced |
| Manufacturer | LATI |
| Trade Name | Latilon |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latilon 28D K/40 PC, 40% Carbon Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate (PC) based compound. Carbon fiber. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0015 cm/cm | 0.00050 - 0.0015 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0015 - 0.0030 cm/cm | 0.0015 - 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa @Temperature 120 °C |
10900 psi @Temperature 248 °F |
|
| 100 MPa @Temperature 90.0 °C |
14500 psi @Temperature 194 °F |
||
| 115 MPa @Temperature 60.0 °C |
16700 psi @Temperature 140 °F |
||
| 135 MPa @Temperature 23.0 °C |
19600 psi @Temperature 73.4 °F |
||
| Elongation at Break | 1.3 % @Temperature 23.0 °C |
1.3 % @Temperature 73.4 °F |
|
| 1.3 % @Temperature 60.0 °C |
1.3 % @Temperature 140 °F |
||
| 1.3 % @Temperature 90.0 °C |
1.3 % @Temperature 194 °F |
||
| 1.4 % @Temperature 120 °C |
1.4 % @Temperature 248 °F |
||
| Tensile Modulus | 14.0 GPa @Temperature 120 °C |
2030 ksi @Temperature 248 °F |
|
| 15.6 GPa @Temperature 90.0 °C |
2260 ksi @Temperature 194 °F |
||
| 16.8 GPa @Temperature 60.0 °C |
2440 ksi @Temperature 140 °F |
||
| 18.0 GPa @Temperature 23.0 °C |
2610 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 1.00 J/cm² | 4.76 ft-lb/in² | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 135 °C | 275 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | |
| Vicat Softening Point | 145 °C @Load 5.00 kg |
293 °F @Load 11.0 lb |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 100 - 120 °C | 212 - 248 °F | |
| Drying Temperature | 120 - 130 °C @Time 10800 sec |
248 - 266 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- RheTech Products FT4650-583UV Thermoplastic Polyolefin, UV Stabilized, Exterior DX9 Black
- Premix Premi-Glas® 1200-20 Fiberglass Reinforced Thermoset SMC
- PolyOne Edgetek® GF 5209 10 FPS 15 BLACK 30 A 1 Acetal-Copolymer, Glass Filled (discontinued **)
- MarkeTech Repton 601 Mullite
- SABIC Innovative Plastics ULTEM 2410EPR PEI (Asia Pacific)
- Shin-Etsu Silicones KBE-3803A Fluid
- Silberline Silvet® 210-30-E1
- Styron CALIBREâ„¢ 301-10 Polycarbonate
- SABIC Innovative Plastics LNP THERMOCOMP MF002S PP (Europe-Africa-Middle East)
- ExxonMobil PP3155 Homopolymer Grade for Nonwoven and Fiber Applications
Copyright © lookpolymers.com All Rights Reserved