Atom Adhesives AA-BOND FDA26 Epoxy Adhesive

Category	Polymer , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer	Atom Adhesives
Trade Name
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Atom Adhesives AA-BOND FDA26 Epoxy Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

AA-BOND FDA26 is Versatile adhesive guaranteed a high strength bond. AA-BOND FDA26 is two part adhesive used and cured at room temperature for bonding, repair applications by manufacturers of food preparation, processing and packaging equipment and devices.Appearance: GrayCure Type: Heat cure or Room TemperatureBenefits:Excellent durabilityHigh shear and peel strengthHeat and impact resistantHandy duo-pack cartridges for easy mixing Mix Ratio by weight: 100:14/Resin:HardenerSubstrates: Most metals, ceramic, glass and plasticsInformation provided by Atom Adhesives

Physical Properties	Metric	English	Comments
Specific Gravity	2.36 g/cc	2.36 g/cc	mixed, uncured
Solids Content	100 %	100 %	reactive, uncured
Viscosity	16500 - 18500 cP	16500 - 18500 cP	uncured

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	86 <br>@Temperature 25.0 °C,<br> Time 86400 sec	86 <br>@Temperature 77.0 °F,<br> Time 24.0 hour	cured
	90 <br>@Temperature 65.0 °C,<br> Time 3600 sec	90 <br>@Temperature 149 °F,<br> Time 1.00 hour	cured
Adhesive Bond Strength	14.6 MPa <br>@Temperature 65.0 °C,<br> Time 3600 sec	2120 psi <br>@Temperature 149 °F,<br> Time 1.00 hour
	15.1 MPa <br>@Temperature 25.0 °C,<br> Time 86400 sec	2190 psi <br>@Temperature 77.0 °F,<br> Time 24.0 hour

Thermal Properties	Metric	English
Maximum Service Temperature, Air	135 °C	275 °F
Minimum Service Temperature, Air	-60.0 °C	-76.0 °F
Glass Transition Temp, Tg	113 °C	235 °F

Processing Properties	Metric	English	Comments
Cure Time	60.0 - 240 min <br>@Temperature 65.0 °C	1.00 - 4.00 hour <br>@Temperature 149 °F
	1440 min <br>@Temperature 25.0 °C	24.0 hour <br>@Temperature 77.0 °F
Pot Life	50.0 min	50.0 min	uncured