BASF Capron® 8334G Impact Modified, 40% Glass-Filled Nylon 6 (Conditioned)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Filled, Impact Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® 8334G Impact Modified, 40% Glass-Filled Nylon 6 (Conditioned)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Capron 8334G is a heat stabilized, 40% glass fiber reinforced polyamide 6 molding compound developed for applications requiring a high level of stiffness combined with excellent impact performance. It is also available in heat stabilized (Capron 8334G HS) and/or pigmented versions.Capron 8334G is generally recommended for applications such as power tool housings and chain saw housings.Data provided by Allied Signal.Processing: Max. water content 0.12%. Product is supplied in sealed containers and drying is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 85°C (185 °F). Is recommended. Drying time is dependent on moisture level.Melt Temperature: 270-295 degC (518-563 degF). Mold Temperature: 80-95 degC (176-203 degF). Injection and Packing Pressure: 35-125 bar (500-1500psi) This product can be processed over a wide range of mold temperatures; however, for applications where aesthetics critical, a mold surface temperature of 80-95 degC (176-203 degF) is required. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Back pressure can be utilized to provide uniform melt consistency and reduce trapped air and gas. A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate. Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
(Dry)
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM Data MD (Dry)
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO Data (Dry)
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 138 MPa
20000 psi
ISO value at 5mm/min.
140 MPa
20300 psi
ASTM data at 5 mm/min.
Tensile Strength, Yield 140 MPa
20300 psi
50 mm/min; Same value from ASTM and ISO test.
Elongation at Break 4.3 %
4.3 %
Nominal
4.5 %
4.5 %
ASTM, 5 mm/minl
Elongation at Yield 4.0 %
4.0 %
ASTM Value at 50 mm/min.
4.1 %
4.1 %
ISO Value at 50 mm/min.
Tensile Modulus 8.97 GPa
1300 ksi
same value from ASTM and ISO test.
Flexural Yield Strength 195 MPa
28300 psi
ASTM Data
Flexural Modulus 6.20 GPa
899 ksi
ASTM Data
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
(Dry)
Processing Properties Metric English Comments
Processing Temperature 275 °C
527 °F
See Materials Notes
Mold Temperature 95.0 °C
203 °F
See Materials Notes
Drying Temperature 85.0 °C
185 °F
See Materials Notes