BASF Polystyrol® 585 K Impact Grade Polystyrene (Europe)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | BASF |
| Trade Name | Polystyrol® |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | BASF Polystyrol® 585 K Impact Grade Polystyrene (Europe).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Special high gloss, high-impact grade for all types of housings. Basis product for gloss capping.Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.0055 cm/cm | 0.0055 in/in | |
| Melt Flow | 4.0 g/10 min <br>@Load 5.00 kg,<br> Temperature 200 °C |
4.0 g/10 min <br>@Load 11.0 lb,<br> Temperature 392 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | |
| Elongation at Break | 25 % | 25 % | |
| Elongation at Yield | 1.9 % | 1.9 % | |
| Tensile Modulus | 1.90 GPa | 276 ksi | |
| Charpy Impact Unnotched | 16.0 J/cm² | 76.1 ft-lb/in² | |
| 8.00 J/cm² <br>@Temperature -30.0 °C |
38.1 ft-lb/in² <br>@Temperature -22.0 °F |
||
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 2000 MPa | 290000 psi | |
| Tensile Creep Modulus, 1000 hours | 1600 MPa | 232000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C <br>@Temperature 20.0 °C |
55.6 µin/in-°F <br>@Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 87.0 °C | 189 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | |
| Vicat Softening Point | 89.0 °C | 192 °F | |
| Flammability, UL94 | HB <br>@Thickness 3.20 mm |
HB <br>@Thickness 0.126 in |
|
| Oxygen Index | 18 % | 18 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | |
| Dielectric Constant | 2.5 <br>@Frequency 100 Hz |
2.5 <br>@Frequency 100 Hz |
|
| 2.5 <br>@Frequency 1e+6 Hz |
2.5 <br>@Frequency 1e+6 Hz |
||
| Dissipation Factor | 0.00040 <br>@Frequency 100 Hz |
0.00040 <br>@Frequency 100 Hz |
|
| 0.00040 <br>@Frequency 1e+6 Hz |
0.00040 <br>@Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 575 V | 575 V |
Users viewing this material also viewed the following:
- Mateck Magnesium Oxide Substrate, MgO
- Lord Adhesives 410 Flexible, High Impact and Peel Resistance, Long Working Time Acrylic Adhesive
- Silberline A-6205
- Teijin Panlite® GN-3410R Improved Mold Release, Glass Fiber Reinforced, Flame Resistant Polycarbonate Resin
- Hexcel® HexPly® F522 Epoxy Resin, T2C145 Carbon Tape
- A. Schulman PP 3475-01 Polypropylene High Melt Homopolymer Polypropylene
- Cytec EN-11 (Conap) Casting, Potting, and Molding Compound
- Ceradyne SEMICORE® S1-5C Specials SmCo5 Samarium Cobalt Magnet
- Bapolene® 2272 Polyethylene, Injection Grade
- Loctite® 661 Retaining Compound
Copyright © lookpolymers.com All Rights Reserved