Covestro Bayblend® ET 1100* Polycarbonate + ABS, Mineral Filled
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Covestro |
| Trade Name | Bayblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Covestro Bayblend® ET 1100* Polycarbonate + ABS, Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Water Absorption | 0.60 % | 0.60 % | Similar to ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | Similar to ISO 62 |
| Melt Flow | 13 g/10 min @Load 5.00 kg, Temperature 260 °C |
13 g/10 min @Load 11.0 lb, Temperature 500 °F |
estimated from MVR using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1/-2 |
| Elongation at Yield | 4.3 % | 4.3 % | ISO 527-1/-2 |
| Tensile Modulus | 3.30 GPa | 479 ksi | ISO 527-1/-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 55.0 µm/m-°C | 30.6 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | ISO 75-1/-2 |
| Vicat Softening Point | 140 °C | 284 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 0.900 mm |
HB @Thickness 0.0354 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Injection Velocity | 240 mm/sec | 9.45 in/sec | ISO 294 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Asia Pacific | |
| Europe | ||
| India | ||
| Near East/Africa | ||
| South and Central America | ||
| Feature | Release agent | |
| Form | Pellets | |
| Process | Profile Extrusion | |
| Sheet Extrusion | ||
| Thermoforming |
Users viewing this material also viewed the following:
- MV Labs CO300 CoCO3 ·xH2O Cobalt(II) carbonate hydrate
- PolyOne LubriOne™ NY-10GF/10T BLACK Polyamide 6 (Nylon 6)
- Polykemi AB POLYform POM C M140 Polyoxymethylene
- PolyOne Geon™ Vinyl Flexible 90450 Polyvinyl Chloride, Flexible (PVC, Flexible)
- SABIC Innovative Plastics GELOY XP7560 ASA (Europe-Africa-Middle East)
- Solvay Specialty Polymers Ryton® R-4-200BL Polyphenylene Sulfide (PPS), 40% Glass Fiber
- Chase Plastics CP Pryme® A130 ABS, 30% Glass Fiber Reinforced
- A. Schulman POLYBLAK™ 4479-01A Black Color Concentrate, 50% Carbon Black Based In Polyethylene
- A. Schulman POLYFORT™ PP 7001
Copyright © lookpolymers.com All Rights Reserved