- Eurostar Staramide AK8ST41 PA66, Mineral Reinforced, Impact Modified, Injection Molding
Eurostar Staramide AK8ST41 PA66, Mineral Reinforced, Impact Modified, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Mineral Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide AK8ST41 PA66, Mineral Reinforced, Impact Modified, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide AK8ST41 is an Impact Modified, Mineral Filled Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.50 % @Temperature 23.0 °C |
0.50 % @Temperature 73.4 °F |
ISO 62-1 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 10 % | 10 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 4.80 GPa | 696 ksi | 1 mm/min; ISO 527 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80x10x4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
33.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
33.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Vicat Softening Point | 245 °C | 473 °F | B/120; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 260 - 280 °C | 500 - 536 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 290 °C | 518 - 554 °F | |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Overview of materials for Polycarbonate, NCG Filled
- LG Chemical Lupox® GP1006FD PBT
- Karina E 880-10/136-A-IS-As White PVC Compound
- Sax Polymers SAXAMID 126F2K4 Nylon 6, Glass Fiber/Bead Filled
- A. Schulman POLYBATCH™ AO-25 Antioxidant Masterbatch Based in LDPE
- Dow Corning P5200 ADHESION PROMOTER, RED
- Chosun Refractories MCC-1 Magnesia Calcia Carbon Brick For Refining Ladle
- DuPont Performance Polymers Zytel® 45HSB NC010 Nylon 66 (Unverified Data**)
- Elisto THERMOSTAR® LD 500 Frame Press Insulation Material
Copyright © lookpolymers.com All Rights Reserved